PA66 CM3003G-30 TORAY JAPAN
Amilan®
Electrical components,OA device
Flame retardant,Glass fiber reinforced
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Mechanical properties | Test Condition | Test Method | TORAY JAPAN/CM3003G-30 |
---|---|---|---|
wear resistance | D1044 | 23 mg/1000 | |
Impact strength of cantilever beam gap | 23℃ | D256 | 85 J/m |
tensile strength | 屈服,23℃ | D638 | 170 Mpa |
elongation at break | 23℃ | D638 | 5 % |
Flexural modulus | 23℃ | D790 | 10.0 GPa |
bending strength | 23℃ | D790 | 270 Mpa |
processability | Test Condition | Test Method | TORAY JAPAN/CM3003G-30 |
---|---|---|---|
Shrinkage rate | 3mmt | 0.6-0.8 % | |
1mmt | 0.2-0.4 % |
physical property | Test Condition | Test Method | TORAY JAPAN/CM3003G-30 |
---|---|---|---|
Water absorption rate | 23℃,水中 | D570 | 5.5 % |
Rockwell hardness | 23℃ | D785 | 121 R |
Water absorption rate | 23℃,24hrs | D570 | 0.6 % |
density | D792 | 1.38 |
Thermal performance | Test Condition | Test Method | TORAY JAPAN/CM3003G-30 |
---|---|---|---|
Heat distortion temperature | 0.46Mpa,HDT | D648 | 262 °C |
melting temperature | DSC | 265 °C | |
Heat distortion temperature | 1.86MPa,HDT | D648 | 255 °C |
UL flame retardant rating | UL 94 | HB |