Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM LT802 ASAHI JAPAN
TENAC™
Engine parts,Household goods,Engineering accessories,Shell
Low friction coefficient,Homopolymer,wear resistant,Lubricity,Anti creep,high viscosity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Mechanical propertiesTest ConditionTest MethodASAHI JAPAN/LT802
bending strengthASTM D790/ISO 17891 kg/cm²(MPa)[Lb/in²]
Flexural modulusASTM D790/ISO 1782650 kg/cm²(MPa)[Lb/in²]
Rockwell hardness-ASTM D78592 M
bending strengthASTM D79091 Mpa
wear resistanceASTM D104413
elongationASTM D638/ISO 52780 %
Rockwell hardness-ASTM D785120 R
Impact strength of cantilever beam gapASTM D256118 J/m
Rockwell hardnessASTM D78592
elongation at breakASTM D63880 %
Flexural modulusASTM D7902650 Mpa
tensile strength ASTM D638/ISO 52764 kg/cm²(MPa)[Lb/in²]
ASTM D63864 Mpa
otherTest ConditionTest MethodASAHI JAPAN/LT802
characteristic对金属有优异的耐摩擦和耐耗
Physical propertiesTest ConditionTest MethodASAHI JAPAN/LT802
densityASTM D792/ISO 11831.42
melt mass-flow rateASTM D1238/ISO 11331.7 g/10min
Water absorption rateASTM D570/ISO 620.2 %
physical property Test ConditionTest MethodASAHI JAPAN/LT802
Shrinkage rate垂直方向旭化成法1.8-2.2 %
平行方向旭化成法1.8-2.2 %
Water absorption rateASTM D5700.2 %
Thermal performanceTest ConditionTest MethodASAHI JAPAN/LT802
Combustibility (rate)UL 94HB
melt mass-flow rateASTM D12381.7 g/10min
Heat distortion temperature0.45MPa，HDTASTM D648172 °C
HDTASTM D648/ISO 75125 ℃（℉）
1.82MPa，HDTASTM D648125 °C
Linear coefficient of thermal expansionASTM D696/ISO 1135910 mm/mm.℃
TMA法10
UL flame retardant ratingUL 94HB