PA6 PX11311 WH9F059 SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Automotive body panels、Automotive sector
Dimensional stability、Low Specific Gravity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/PX11311 WH9F059 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 199 °C |
| Specific Heat | ASTMC351 | 1420 J/kg/°C | |
| Linear thermal expansion coefficient | MD:-40到40°C | ASTME831 | 3.1E-05 cm/cm/°C |
| MD:40到120°C | 1.9E-05 cm/cm/°C | ||
| ASTM D790/ISO 178 | 2.1 W/m/K | ||
| Linear thermal expansion coefficient | TD:-40到40°C | ASTME831 | 4.6E-05 cm/cm/°C |
| TD:40到120°C | 7E-05 cm/cm/°C | ||
| ISO22007-2 | 1.4 W/m/K |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/PX11311 WH9F059 |
|---|---|---|---|
| 内部方法 | 0.25 % | ||
| Equilibrium,23°C,50%RH | ISO62 | 0.040 % | |
| Melt Volume flow Rate | 300°C/10.0kg | ISO1133 | 49.0 cm3/10min |
| Modeling Shrinkage | TD:24小时 | ASTMD955 | 0.48 % |
| MD:24小时 | 0.33 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/PX11311 WH9F059 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 9050 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 2.0 % |
| Tensile Modulus | 7240 Mpa | ||
| Tensile Strength | 断裂 | 52.0 Mpa | |
| Flexural Strength | 断裂,50.0mm跨距 | ASTMD790 | 76.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/PX11311 WH9F059 |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO179 | 5.3到18 kJ/m² | |
| Unnotched Izod Impact Strength | 23°C | ASTMD4812 | 180 J/m |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/PX11311 WH9F059 |
|---|---|---|---|
| Glow Wire Ignition Temperature | 1.00mm | IEC60695-2-13 | 775 °C |
| Glow Wire Flammability Index | 2.00mm | IEC60695-2-12 | 960 °C |
| Glow Wire Ignition Temperature | 3.00mm | IEC60695-2-13 | 850 °C |
| Flame Rating | 1.00mm | UL94 | V-0 |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/PX11311 WH9F059 |
|---|---|---|---|
| Surface Resistivity | ASTMD257 | >1.0E+15 ohms | |
| High Amp Arc Ignition | HAI | UL746 | PLC 0 |
| Dielectric Strength | 1.00mm,inOil | ASTMD149 | >10 KV/mm |
| Comparative Tracking Index | IEC60112 | 600 V | |
| Dielectric Constant | 1.10GHz | ASTMES7-83 | 4.74 |
| Dissipation Factor? | 7.7E-03 | ||
| Hot-wire Ignition | HWI | UL746 | PLC 0 |