PBT+ASA Generic PBT+ASA - Glass Fiber Generic
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | Generic/Generic PBT+ASA - Glass Fiber |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179 | 6.0to10 kJ/m² |
Suspended wall beam without notch impact strength | 23°C | ISO 180 | 40to50 kJ/m² |
Impact strength of cantilever beam gap | 23°C | ISO 180 | 9.9to11 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179 | 39to55 kJ/m² |
Electrical performance | Test Condition | Test Method | Generic/Generic PBT+ASA - Glass Fiber |
---|---|---|---|
Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 | |
relative permittivity | 23°C | IEC 60250 | 3.65 |
Dissipation Factor | 23°C | IEC 60250 | 3.0E-3到0.021 |
Volume resistivity | 23°C | IEC 60093 | 1.0E+13到2.0E+15 ohms·cm |
Surface Resistivity | IEC 60093 | 1.0E+14到1.0E+16 ohms |
Mechanical properties | Test Condition | Test Method | Generic/Generic PBT+ASA - Glass Fiber |
---|---|---|---|
Flexural modulus | 23°C | ISO 178 | 4010to9800 MPa |
Tensile strain | 断裂,23°C | ISO 527-2 | 2.0to3.0 % |
Tensile modulus | 23°C | ISO 527-2 | 4910to10200 MPa |
tensile strength | 断裂,23°C | ISO 527-2 | 98.3to126 MPa |
bending strength | 23°C | ISO 178 | 139to200 MPa |
flammability | Test Condition | Test Method | Generic/Generic PBT+ASA - Glass Fiber |
---|---|---|---|
Hot filament ignition temperature | IEC 60695-2-13 | 675to775 °C | |
Burning wire flammability index | IEC 60695-2-12 | 650to960 °C |
physical property | Test Condition | Test Method | Generic/Generic PBT+ASA - Glass Fiber |
---|---|---|---|
Melt volume flow rate | 275°C/2.16kg | ISO 1133 | 19.7to35.1 cm³/10min |
Shrinkage rate | 23°C | ISO 294-4 | 0.18to1.1 % |
density | 23°C | ISO 1183 | 1.30to1.51 g/cm³ |
Apparent density | ISO 60 | 0.70to0.85 g/cm³ | |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.10to0.20 % |
饱和,23°C | ISO 62 | 0.40 % |
Thermal performance | Test Condition | Test Method | Generic/Generic PBT+ASA - Glass Fiber |
---|---|---|---|
melting temperature | ISO 11357-3 | 220to243 °C | |
vicat | ISO 306 | 143to215 °C | |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 204to220 °C |
1.8MPa,未退火,HDT | ISO 75-2/A | 148to200 °C | |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.0E-5到4.0E-5 cm/cm/°C |