PC/ABS AC2000 FCFC TAIWAN
TAIRILOY®
Electrical field、Electronic field、Automotive sector、Medical packaging
heat-resisting、Toughening、High impact resistance
TDS
Processing
MSDS
UL
RoHS
SVHC
PSC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | FCFC TAIWAN/AC2000 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.18mm | ISO 180 | 590 J/m |
| 23°C,3.18mm | ASTM D256 | 590 J/m |
| hardness | Test Condition | Test Method | FCFC TAIWAN/AC2000 |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ASTM D785 | 112 |
| R计秤,23°C | ISO 2039-2 | 112 |
| Mechanical properties | Test Condition | Test Method | FCFC TAIWAN/AC2000 |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 89.0 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 54.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 2450 Mpa |
| bending strength | 23°C | ASTM D790 | 89.0 Mpa |
| Flexural modulus | 23°C | ASTM D790 | 2450 Mpa |
| tensile strength | 23°C | ASTM D638 | 53.9 Mpa |
| flammability | Test Condition | Test Method | FCFC TAIWAN/AC2000 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | FCFC TAIWAN/AC2000 |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.15 g/cm³ |
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.40-0.60 % |
| melt mass-flow rate | 240°C/5.0kg | ISO 1133 | 7.0 g/10min |
| 240°C/5.0kg | ASTM D1238 | 7.0 g/10min | |
| density | ASTM D792 | 1.15 g/cm³ |
| Thermal performance | Test Condition | Test Method | FCFC TAIWAN/AC2000 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.35mm，HDT | ASTM D648 | 106 °C |
| 1.8MPa,Unannealed,6.35mm，HDT | ISO 75-2/A | 106 °C |