Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC GS2030N1D BK9001 MITSUBISHI ENGINEERING JAPAN
IUPILON™
fibre
Flame retardant,enhance,Filler: Glass fiber reinf,30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GS2030N1D BK9001 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 45 kJ/m² |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GS2030N1D BK9001 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 9000 Mpa | |
| bending strength | ISO 178 | 175 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.5 % |
| Flexural modulus | ISO 178 | 8500 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 103 Mpa |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GS2030N1D BK9001 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GS2030N1D BK9001 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GS2030N1D BK9001 |
|---|---|---|---|
| Shrinkage rate | TD:3.20mm | 0.25-0.45 % | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 4.80 cm3/10min |
| Shrinkage rate | MD:3.20mm | 0.050-0.25 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.090 % |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 5.7 g/10min |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GS2030N1D BK9001 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 148 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 145 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.8E-05 cm/cm/°C |
| TD | ISO 11359-2 | 6.3E-05 cm/cm/°C |