Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC GSH2030FTR MITSUBISHI ENGINEERING JAPAN
IUPILON™
Automotive Applications、electrical equipment
Glass fiber reinforced、Filler: Glass fiber reinf、30% filler by weight、30% filler by weight
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GSH2030FTR |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 4.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 32 kJ/m² |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GSH2030FTR |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 6200 Mpa | |
| bending strength | ISO 178 | 126 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.5 % |
| Flexural modulus | ISO 178 | 5800 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 75.0 Mpa |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GSH2030FTR |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 4 |
| flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GSH2030FTR |
|---|---|---|---|
| UL flame retardant rating | 0.40mm | UL 94 | HB |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GSH2030FTR |
|---|---|---|---|
| Shrinkage rate | TD:3.20mm | 0.15-0.35 % | |
| Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 5.20 cm3/10min |
| Shrinkage rate | MD:3.20mm | 0.15-0.35 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.090 % |
| density | ISO 1183 | 1.43 g/cm³ | |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 7.0 g/10min |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/GSH2030FTR |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 145 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 139 °C |