PA6 B3GF50 AKRO-PLASTIC GERMANY
AKROMID®
engineering application
Filler: Glass fiber reinf、50% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | AKRO-PLASTIC GERMANY/B3GF50 |
---|---|---|---|
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 100 kJ/m² |
-30°C | ISO 179/1eU | 90 kJ/m² |
hardness | Test Condition | Test Method | AKRO-PLASTIC GERMANY/B3GF50 |
---|---|---|---|
ball-indentation hardness | H961/30 | ISO 2039-1 | 270 Mpa |
Supplementary Information | Test Condition | Test Method | AKRO-PLASTIC GERMANY/B3GF50 |
---|---|---|---|
ReinforcementContent | ISO 1172 | 50 % |
Electrical performance | Test Condition | Test Method | AKRO-PLASTIC GERMANY/B3GF50 |
---|---|---|---|
Volume resistivity | IEC 60093 | 1E+13 ohms·cm | |
Surface Resistivity | IEC 60093 | 1E+12 ohms | |
Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
Mechanical properties | Test Condition | Test Method | AKRO-PLASTIC GERMANY/B3GF50 |
---|---|---|---|
Tensile modulus | ISO 527-2/1 | 17000 Mpa | |
tensile strength | 断裂 | ISO 527-2/5 | 240 Mpa |
bending strength | ISO 178 | 340 Mpa | |
Flexural modulus | ISO 178 | 14900 Mpa | |
Tensile strain | 断裂 | ISO 527-2/5 | 2.5 % |
flammability | Test Condition | Test Method | AKRO-PLASTIC GERMANY/B3GF50 |
---|---|---|---|
burning rate | 1.00mm | FMVSS302 | <100 mm/min |
Burning wire flammability index | 1.6mm | IEC 60695-2-12 | 650 °C |
UL flame retardant rating | 1.6mm | UL 94 | HB |
physical property | Test Condition | Test Method | AKRO-PLASTIC GERMANY/B3GF50 |
---|---|---|---|
Shrinkage rate | TD | ISO 294-4 | 0.90 % |
MD | ISO 294-4 | 0.20 % | |
moisture absorption | 70°C,62%RH | ISO 1110 | 1.3to1.6 % |
spiral flow length | 内部方法 | 43.0 CM | |
Water absorption rate | 饱和,23°C | ISO 62 | 4.5to5.1 % |
Thermal performance | Test Condition | Test Method | AKRO-PLASTIC GERMANY/B3GF50 |
---|---|---|---|
TemperatureIndex | 50%LossofTensileStrength,20000hr | IEC 216 | 130to150 °C |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 220 °C |
melting temperature | DIN EN11357-1 | 220 °C | |
TemperatureIndex | 50%LossofTensileStrength,5000hr | IEC 216 | 160to175 °C |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 220 °C |
Linear coefficient of thermal expansion | MD:23到80°C | ISO 11359-2 | 1.1E-05 cm/cm/°C |
Heat distortion temperature | 8.0MPa,未退火,HDT | ISO 75-2/C | 185 °C |
Linear coefficient of thermal expansion | TD:23to80°C | ISO 11359-2 | 9.4E-05 cm/cm/°C |