Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBAT C1200 BASF GERMANY
ECOFLEX®
chip、Bag、cast film 、compost product 、Blow film、Agricultural applications
Semi crystalline、Good printability、aromatic、high molecular weight、Food contact、Biodegradable、Easy to process、Good tensile performance、Good thermal stability、welding、compostable
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | BASF GERMANY/C1200 |
|---|---|---|---|
| FailureEnergy-DynaTest | 50.0µm | DIN 53373 | 240 J/cm |
| hardness | Test Condition | Test Method | BASF GERMANY/C1200 |
|---|---|---|---|
| Shore hardness | 邵氏D | ISO 868 | 32 |
| film | Test Condition | Test Method | BASF GERMANY/C1200 |
|---|---|---|---|
| elongation | MD:断裂,50µm,吹塑薄膜 | ISO 527-3 | 560 % |
| OTr | 23°C,0%RH,50µm,吹塑薄膜 | ASTM D3985 | 1200 cm³/m²/24hr |
| Water Vapor Transmission Rate | 23°C,85%RH,50µm,吹塑薄膜 | ASTMF1249 | 140 g/m²/24hr |
| tensile strength | MD:断裂,50µm,吹塑薄膜 | ISO 527-3 | 36.0 Mpa |
| film thickness | 50 µm | ||
| tensile strength | TD:50µm,吹塑薄膜 | ISO 527-3 | 44.0 Mpa |
| elongation | TD:断裂,50µm,吹塑薄膜 | ISO 527-3 | 710 % |
| tensile strength | TD:断裂,50µm,吹塑薄膜 | ISO 527-3 | 45.0 Mpa |
| MD:50µm,吹塑薄膜 | ISO 527-3 | 35.0 Mpa |
| optical performance | Test Condition | Test Method | BASF GERMANY/C1200 |
|---|---|---|---|
| transmissivity | 50.0µm,吹塑薄膜 | ASTM D1003 | 82.0 % |
| physical property | Test Condition | Test Method | BASF GERMANY/C1200 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 2.50to4.50 cm3/10min |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 2.7to4.9 g/10min |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/C1200 |
|---|---|---|---|
| vicat | ISO 306/A50 | 91.0 °C | |
| melting temperature | DSC | 110to120 °C |