Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC GSH2010KR 9001 MITSUBISHI ENGINEERING JAPAN
IUPILON™ 
Automotive Applications,electrical equipment
Glass fiber reinforced,Filler: Glass fiber reinf,10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/GSH2010KR 9001
Impact strength of simply supported beam without notch23°CISO 17968 kJ/m²
Mechanical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/GSH2010KR 9001
Tensile modulusISO 527-24200 Mpa
bending strengthISO 178120 Mpa
Tensile strain断裂ISO 527-23.4 %
Flexural modulusISO 1783500 Mpa
tensile strength 断裂ISO 527-275.0 Mpa
Electrical performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/GSH2010KR 9001
Compared to the Leakage Tracking Index (CTI)CTIUL 746PLC 3
flammabilityTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/GSH2010KR 9001
UL flame retardant rating0.40mmUL 94HB
physical property Test ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/GSH2010KR 9001
Shrinkage rateTD:3.20mm0.40-0.60 %
Melt volume flow rate300°C/1.2kgISO 113311.0 cm3/10min
Shrinkage rate吸水率(饱和,23°C)0.14 %
MD:3.20mm0.30-0.50 %
melt mass-flow rate300°C/1.2kgISO 113312 g/10min
Thermal performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/GSH2010KR 9001
Heat distortion temperature0.45MPa,未退火,HDTISO 75-2/B139 °C
1.8MPa,未退火,HDTISO 75-2/A134 °C
Linear coefficient of thermal expansionMDISO 11359-24E-05 cm/cm/°C
TDISO 11359-26.7E-05 cm/cm/°C