PC+TPU II 55D DSM Additive Manufacturing
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | DSM Additive Manufacturing/II 55D |
|---|---|---|---|
| Shore hardness | 邵氏D | ASTM D2240 | 56 |
| Mechanical properties | Test Condition | Test Method | DSM Additive Manufacturing/II 55D |
|---|---|---|---|
| Taber abraser | 1000Cycles,1000g,H-18转轮 | ASTM D1044 | 11.0 mg |
| tensile strength | 100%应变 | ASTM D1708 | 18.1 MPa |
| Flexural modulus | ASTM D790 | 95.1 MPa | |
| coefficient of friction | 与自身-动态 | ASTM D1894 | 0.46 |
| tensile strength | 300%应变 | ASTM D1708 | 49.0 MPa |
| bending strength | 5.0%应变 | ASTM D790 | 3.52 MPa |
| tensile strength | 50%应变 | ASTM D1708 | 13.6 MPa |
| elongation | 断裂 | ASTM D1708 | 370 % |
| tensile strength | 断裂 | ASTM D1708 | 61.8 MPa |
| Electrical performance | Test Condition | Test Method | DSM Additive Manufacturing/II 55D |
|---|---|---|---|
| dielectric constant | 60Hz | ASTM D150 | 3.71 |
| dielectric strength | ASTM D149 | 17 kV/mm |
| physical property | Test Condition | Test Method | DSM Additive Manufacturing/II 55D |
|---|---|---|---|
| Water absorption rate | 饱和 | ASTM D750 | 0.54 % |
| Shrinkage rate | MD | ASTM D955 | 0.80to2.3 % |
| melt mass-flow rate | ASTM D1238 | 35 g/10min | |
| average molecular weight | 内部方法 | 231000 Mw |
| Thermal performance | Test Condition | Test Method | DSM Additive Manufacturing/II 55D |
|---|---|---|---|
| vicat | ASTM D1525 | 107 °C | |
| Glass Transition Temperature | ASTME1356 | 1.00 °C | |
| melting temperature | ASTME1356 | 180 °C |