Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPA HTN53G60LRHF DUPONT SHENZHEN
Zytel®
Electronic and Electrical Applications,Automotive components
High mobility,High rigidity,lubrication,Filler: Glass fiber reinf,60% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT SHENZHEN/HTN53G60LRHF |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 7.892to21.357 |
| Suspended wall beam without notch impact strength | 23℃ | J/m | 0.085to0.462 |
| hardness | Test Condition | Test Method | DUPONT SHENZHEN/HTN53G60LRHF |
|---|---|---|---|
| Rockwell hardness | 23℃ | 122to125 |
| Mechanical properties | Test Condition | Test Method | DUPONT SHENZHEN/HTN53G60LRHF |
|---|---|---|---|
| Yield, 23 ℃ | 27.03to260.0 MPa | ||
| % | 1.5-5.0 | ||
| Fracture, 23 ℃ | 26.0to260.0 MPa | ||
| % | 2.0-4.6 |
| Electrical performance | Test Condition | Test Method | DUPONT SHENZHEN/HTN53G60LRHF |
|---|---|---|---|
| dielectric strength | 23℃ | V/mil | 490to610 |
| Surface Resistivity | ohms | 1.0E+12-1.0E+14 | |
| Compared to the Leakage Tracking Index (CTI) | V | ||
| Volume resistivity | 23℃ | ohms·cm | 1.0E+4-1.0E+16 |
| physical property | Test Condition | Test Method | DUPONT SHENZHEN/HTN53G60LRHF |
|---|---|---|---|
| Flow: 23 ℃ | 流动,23℃ | mm/mm | 25.4E-3-134.6E-3 |
| Water absorption rate | 23℃,24hr | % | 0.15-0.53 |
| Thermal performance | Test Condition | Test Method | DUPONT SHENZHEN/HTN53G60LRHF |
|---|---|---|---|
| 0.45MPa, Not annealed | °C | 137to223 | |
| 1.8MPa, Not annealed | °C | 223to270 | |
| melting temperature | °C | 220to265 | |
| Linear coefficient of thermal expansion | MD | mm/mm/°C | 30.5E-5到50.8E-5 |