Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC DF-1002 BK8-229 SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Electronic and Electrical Applications,Plastic bag,Medical and nursing supplies
Easy to form,Easy to demould,Filler: Glass fiber reinf,10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/DF-1002 BK8-229 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 55 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 18.4 J |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 10.5 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 8.7 kJ/m² |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/DF-1002 BK8-229 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-30to30°C | ASTM D696 | 5.3E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 141 °C |
| 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 146 °C | |
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTM D696 | 4.6E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 54.9 °C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DF-1002 BK8-229 |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-2/5 | 5.7 % |
| tensile strength | 断裂 | ISO 527-2/5 | 74.0 Mpa |
| Tensile modulus | ASTM D638 | 4250 Mpa | |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 4110 Mpa |
| elongation | 断裂 | ASTM D638 | 5.6 % |
| tensile strength | 屈服 | ASTM D638 | 81.0 Mpa |
| 屈服 | ISO 527-2/5 | 80.0 Mpa | |
| Tensile modulus | ISO 527-2/1 | 4170 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/5 | 3.8 % |
| elongation | 屈服 | ASTM D638 | 3.9 % |
| tensile strength | 断裂 | ASTM D638 | 75.0 Mpa |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 138 Mpa |
| flexural modulus | ISO 178 | 3960 Mpa |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DF-1002 BK8-229 |
|---|---|---|---|
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.14 % |
| shrinkage rate | MD：24小时 | ASTM D955 | 0.40-0.60 % |
| TD：24hr | ASTM D955 | 0.60-0.80 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |