ABS M203FC 000000 ELIX POLYMERS SPANISH
--
medical care、Shell
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Other performance | Test Condition | Test Method | ELIX POLYMERS SPANISH/M203FC 000000 |
---|---|---|---|
melting temperature | ISO 294 | 240 °C | |
burning rate | ISO 3795 | 60 mm/min | |
injection speed | ISO 294 | 240 mm/sec |
hardness | Test Condition | Test Method | ELIX POLYMERS SPANISH/M203FC 000000 |
---|---|---|---|
ball-indentation hardness | ISO 2039-1 | 110 Mpa |
Electrical performance | Test Condition | Test Method | ELIX POLYMERS SPANISH/M203FC 000000 |
---|---|---|---|
Dissipation Factor | IEC 60250 | 0.09 | |
dielectric constant | IEC 60250 | 3 100HZ | |
Dissipation Factor | 相对漏电起痕指数 | IEC 60112 | 600 V |
dielectric strength | 1.00mm | IEC 60243-1 | 35 KV/mm |
dielectric constant | IEC 60250 | 2.9 1MHz | |
Surface Resistivity | IEC 60093 | 1E+15 Ω.cm | |
Volume resistivity | IEC 60093 | 1E+13 Ω.cm |
Mechanical properties | Test Condition | Test Method | ELIX POLYMERS SPANISH/M203FC 000000 |
---|---|---|---|
bending strength | 23°C | ISO 178 | 70 Mpa |
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 7 kJ/m² |
23°C | ISO 179/1eA | 15 kJ/m² | |
Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 15 kJ/m² |
elongation at break | 屈服,23°C | ISO 527-2 | 2.6 % |
Flexural modulus | 23°C | ISO 178 | 2400 Mpa |
tensile strength | 屈服,23°C | ISO 527-2 | 46 Mpa |
Tensile modulus | 23°C | ISO 527-2 | 2400 Mpa |
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 90 kJ/m² |
elongation at break | 23°C | ISO 527-2 | >=15 % |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 110 kJ/m² |
Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 7 kJ/m² |
Flame retardant performance | Test Condition | Test Method | ELIX POLYMERS SPANISH/M203FC 000000 |
---|---|---|---|
GWIT | 2.00mm | IEC 60695-2-12 | 700 °C |
physical property | Test Condition | Test Method | ELIX POLYMERS SPANISH/M203FC 000000 |
---|---|---|---|
melt mass-flow rate | 线性收缩率 | ISO 294-4 | 0.4-0.7 % |
220℃/10.0Kg | ISO 1133 | 31 g/10min |
Thermal performance | Test Condition | Test Method | ELIX POLYMERS SPANISH/M203FC 000000 |
---|---|---|---|
Heat distortion temperature | 1.80MPa退火,HDT | ISO 75-2/Af | 94 °C |
0.45MPa未退火,HDT | ISO 75-2/Bf | 98 °C | |
vicat | 5.10kg | ISO 306/A50 | 99 °C |