Product Name / Manufacturer / Model

Brand

Typical Applications

Properties

Color

Form

Processing Methods

Grade

Filler

Recycled Content

Certificates

Reference Price

PBT
PBT SABIC INNOVATIVE NANSHA 420-1001
Injection grade
US$ 3,620 / MT
FOB Guangzhou port, China
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/420-1001
UL flame retardant rating0.8mmUL 94HB
Extreme Oxygen IndexASTM D286319 %
Burning wire flammability index1.0mmIEC 60695-2-12750 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/420-1001
bending strengthISO 178195 Mpa
Tensile strainBreakISO 527-2/52.0 %
BreakASTM D6382.7 %
Tensile modulusASTM D6389300 Mpa
bending strengthBreak,50.0mmSpanASTM D790190 Mpa
Yield,50.0mmSpanASTM D790195 Mpa
tensile strengthBreakASTM D638120 Mpa
YieldISO 527-2/5125 Mpa
Bending modulusISO 1788500 Mpa
Tensile strainYieldISO 527-2/52.0 %
Bending modulus50.0mmSpanASTM D7907580 Mpa
Tensile modulusISO 527-2/19300 Mpa
tensile strengthBreakISO 527-2/5125 Mpa
Tensile strainYieldASTM D6382.7 %
tensile strengthYieldASTM D638120 Mpa
Taber abraser1000Cycles,1000g,CS-17WheelASTM D104419.0 mg
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/420-1001
Shrinkage rateTD：--3Internal Method0.40-0.60 %
TD：--2Internal Method0.50-1.0 %
TD：--5Internal Method0.60-0.90 %
Water absorption rate24hrASTM D5700.090 %
Specific volumeASTM D7920.660 cm³/g
melt mass-flow rate250°C/2.16kgISO 113317 g/10min
Shrinkage rateTD：3.20mmInternal Method0.50-1.0 %
MD：--4Internal Method0.50-0.80 %
MD：--3Internal Method0.30-0.50 %
MD：--2Internal Method0.30-0.70 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.080 %
Melt Volume Flow Rate (MVR)250°C/2.16kgISO 113313.0 cm3/10min
Shrinkage rateMD：3.20mmInternal Method0.30-0.80 %
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/420-1001
Dielectric strength1.60mm,in OilASTM D14925 KV/mm
Dissipation factor50HzIEC 602501E-03
100HzIEC 602501E-03
Relative permittivity50HzIEC 602503.10
Dielectric strength1.00mm15IEC 60243-119 KV/mm
Volume resistivityIEC 60093>1.0E+15 ohms·cm
Compared to the anti leakage trace indexCTIUL 746PLC 0
Dissipation factor60HzIEC 602501E-03
1MHzIEC 602500.010
Surface resistivityIEC 60093>1.0E+15 ohms
Relative permittivity60HzIEC 602503.10
1MHzIEC 602503.10
Dielectric constant100HzASTM D1503.80
High voltage arc tracing rateHVTRUL 746PLC 1
Dissipation factor1MHzASTM D1500.020
Dielectric strength3.20mm,in OilIEC 60243-116 KV/mm
Volume resistivityASTM D257>3.2E+16 ohms·cm
Arc resistanceASTM D495PLC 5
Dielectric strength3.20mm,inAirASTM D14919 KV/mm
1.60mm,in OilIEC 60243-124 KV/mm
Dissipation factor100HzASTM D1502E-03
Dielectric strength0.800mm,in OilIEC 60243-128 KV/mm
Dielectric constant1MHzASTM D1503.70
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/420-1001
Linear coefficient of thermal expansionTD：-40to40°CASTME8311.2E-04 cm/cm/°C
Ball Pressure Test125°CIEC 60695-10-2Pass
Hot deformation temperature0.45MPa,Unannealed,64.0mmSpanISO 75-2/Bf217 °C
RTI StrUL 746140 °C
Vicat softening temperatureASTM D152514215 °C
Linear coefficient of thermal expansionTD：-40to40°CISO 11359-21.2E-04 cm/cm/°C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af204 °C
1.8MPa,Unannealed,3.20mmASTM D648203 °C
Vicat softening temperature--ISO 306/B50215 °C
Hot deformation temperature1.8MPa,Unannealed,6.40mmASTM D648207 °C
Linear coefficient of thermal expansionMD：60to138°CASTME8312.5E-05 cm/cm/°C
MD：-40to40°CISO 11359-22.5E-05 cm/cm/°C
Hot deformation temperature0.45MPa,Unannealed,6.40mmASTM D648216 °C
Linear coefficient of thermal expansionMD：-40to40°CASTME8312.5E-05 cm/cm/°C
RTI ElecUL 746140 °C
RTI ImpUL 746140 °C
Vicat softening temperature--ISO 306/A50223 °C
thermal conductivityISO 83020.19 W/m/K
Vicat softening temperature--ISO 306/B120215 °C
Hot deformation temperature0.45MPa,Unannealed,3.20mmASTM D648220 °C
impact performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/420-1001
Impact strength of simply supported beam without notch-30°CISO 179/1eU45 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180/1U45 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA5.0 kJ/m²
Impact strength of cantilever beam gap23°CISO 180/1A8.0 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU45 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA5.0 kJ/m²
Dart impact23°C,TotalEnergyASTM D37638.00 J
Impact strength of cantilever beam gap-30°CISO 180/1A7.0 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U45 kJ/m²
hardnessTest ConditionTest MethodSABIC INNOVATIVE NANSHA/420-1001
Rockwell hardnessR-ScaleASTM D785118
Ball Pressure TestH358/30ISO 2039-1122 Mpa
Rockwell hardnessR-ScaleISO 2039-2118
Supplementary InformationTest ConditionTest MethodSABIC INNOVATIVE NANSHA/420-1001
Filling materialASTM D22930 %

Supplier Join

Contact Us

Get App

Top

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index

+86 0755 27873515

Room 906, Global Digital Building, No. 9 Gaoxin Middle 3rd Road, Maling Community, Yuehai Subdistrict, Nanshan District, Shenzhen, Guangdong Province, China