PBT 420-1001 SABIC INNOVATIVE NANSHA

VALOX™

Lawn equipment,Garden equipment,Industrial applications,Automotive External Parts,Electrical field,Electronic field,Architectural application field,Outdoor applications,Electrical appliances,Engine hood parts,Medical supplies,Nursing supplies,Plastic bag,Automotive interior parts,Casters,Household goods,Petroleum Applications,Natural gas supplies,sporting goods,Textile application,Lighting applications

Glass fiber reinforced,dimensional stability ,High rigidity,high strength,heat-resisting

Plastic Datasheets

hardness	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/420-1001
Ball Pressure Test	H358/30	ISO 2039-1	122 Mpa
Rockwell hardness	R-Scale	ASTM D785	118
Rockwell hardness		R-Scale	ISO 2039-2	118

Supplementary Information	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/420-1001
Filling material		ASTM D229	30 %

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/420-1001
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	203 °C
		1.8MPa,Unannealed,6.40mm	ASTM D648	207 °C
		1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	204 °C
		0.45MPa,Unannealed,3.20mm	ASTM D648	220 °C
		0.45MPa,Unannealed,6.40mm	ASTM D648	216 °C
		0.45MPa,Unannealed,64.0mmSpan	ISO 75-2/Bf	217 °C
Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	1.2E-04 cm/cm/°C
		MD：-40to40°C	ASTME831	2.5E-05 cm/cm/°C
		TD：-40to40°C	ASTME831	1.2E-04 cm/cm/°C
		MD：-40to40°C	ISO 11359-2	2.5E-05 cm/cm/°C
		MD：60to138°C	ASTME831	2.5E-05 cm/cm/°C
RTI Elec		UL 746	140 °C
RTI Imp		UL 746	140 °C
RTI Str		UL 746	140 °C
thermal conductivity		ISO 8302	0.19 W/m/K
Vicat softening temperature		ASTM D152514	215 °C
		--	ISO 306/B120	215 °C
		--	ISO 306/B50	215 °C
		--	ISO 306/A50	223 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/420-1001
Bending modulus	50.0mmSpan	ASTM D790	7580 Mpa
Bending modulus			ISO 178	8500 Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	195 Mpa
			ISO 178	195 Mpa
		Break,50.0mmSpan	ASTM D790	190 Mpa
Taber abraser	1000Cycles,1000g,CS-17Wheel	ASTM D1044	19.0 mg
Tensile modulus		ASTM D638	9300 Mpa
Tensile modulus			ISO 527-2/1	9300 Mpa
Tensile strain	Break	ISO 527-2/5	2.0 %
		Yield	ASTM D638	2.7 %
		Yield	ISO 527-2/5	2.0 %
		Break	ASTM D638	2.7 %
tensile strength	Break	ISO 527-2/5	125 Mpa
		Yield	ASTM D638	120 Mpa
		Yield	ISO 527-2/5	125 Mpa
		Break	ASTM D638	120 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/420-1001
Arc resistance		ASTM D495	PLC 5
Compared to the anti leakage trace index		IEC 60112	V
Compared to the anti leakage trace index		CTI	UL 746	PLC 0
Dielectric constant	100Hz	ASTM D150	3.80
Dielectric constant		1MHz	ASTM D150	3.70
Dielectric strength	3.20mm,in Oil	IEC 60243-1	16 KV/mm
		3.20mm,inAir	ASTM D149	19 KV/mm
		1.00mm15	IEC 60243-1	19 KV/mm
		1.60mm,in Oil	IEC 60243-1	24 KV/mm
		0.800mm,in Oil	IEC 60243-1	28 KV/mm
		1.60mm,in Oil	ASTM D149	25 KV/mm
Dissipation factor	1MHz	IEC 60250	0.010
		50Hz	IEC 60250	1E-03
		100Hz	ASTM D150	2E-03
		1MHz	ASTM D150	0.020
		100Hz	IEC 60250	1E-03
		60Hz	IEC 60250	1E-03
High voltage arc tracing rate	HVTR	UL 746	PLC 1
Relative permittivity	60Hz	IEC 60250	3.10
		1MHz	IEC 60250	3.10
		50Hz	IEC 60250	3.10
Surface resistivity		IEC 60093	>1.0E+15 ohms
Volume resistivity		ASTM D257	>3.2E+16 ohms·cm
Volume resistivity			IEC 60093	>1.0E+15 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/420-1001
melt mass-flow rate	250°C/2.16kg	ISO 1133	17 g/10min
Melt Volume Flow Rate (MVR)	250°C/2.16kg	ISO 1133	13.0 cm3/10min
Shrinkage rate	TD：--2	Internal Method	0.50-1.0 %
		MD：--4	Internal Method	0.50-0.80 %
		TD：3.20mm	Internal Method	0.50-1.0 %
		MD：3.20mm	Internal Method	0.30-0.80 %
		MD：--2	Internal Method	0.30-0.70 %
		MD：--3	Internal Method	0.30-0.50 %
		TD：--3	Internal Method	0.40-0.60 %
		TD：--5	Internal Method	0.60-0.90 %
Specific volume		ASTM D792	0.660 cm³/g
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.080 %
Water absorption rate		24hr	ASTM D570	0.090 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/420-1001
Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.0 kJ/m²
Charpy Notched Impact Strength		-30°C	ISO 179/1eA	5.0 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	8.00 J
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	7.0 kJ/m²
Impact strength of cantilever beam gap		23°C	ISO 180/1A	8.0 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	45 kJ/m²
Impact strength of simply supported beam without notch		23°C	ISO 179/1eU	45 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	45 kJ/m²
Suspended wall beam without notch impact strength		-30°C	ISO 180/1U	45 kJ/m²

flammability	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/420-1001
Burning wire flammability index	1.0mm	IEC 60695-2-12	750 °C
Extreme Oxygen Index		ASTM D2863	19 %
UL flame retardant rating	0.8mm	UL 94	HB