Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM TF-30 CF2003 DAICEL MALAYSIA
DURACON®
Fitness equipment,Automotive Applications
wear resistant,High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | DAICEL MALAYSIA/TF-30 CF2003 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 45 |
| Supplementary Information | Test Condition | Test Method | DAICEL MALAYSIA/TF-30 CF2003 |
|---|---|---|---|
| ColorNumber | CF2002/CF2003 |
| Mechanical properties | Test Condition | Test Method | DAICEL MALAYSIA/TF-30 CF2003 |
|---|---|---|---|
| Wear factor | 0.060MPa,0.15m/sec7 | JISK7218 | 1500 10^-8mm³/N·m |
| 0.060MPa,0.15m/sec6 | JISK7218 | 300 10^-8mm³/N·m | |
| Tensile modulus | ISO 527-2 | 1300 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 75 % | |
| coefficient of friction | 与钢-动态3 | JISK7218 | 0.80 |
| Wear factor | 0.49MPa,0.30m/sec4 | JISK7218 | <1.0 10^-8mm³/N·m |
| bending strength | ISO 178 | 43.0 Mpa | |
| Wear factor | 0.49MPa,0.30m/sec5 | JISK7218 | 200 10^-8mm³/N·m |
| Flexural modulus | ISO 178 | 1200 Mpa | |
| coefficient of friction | Dynamic2 | JISK7218 | 0.58 |
| tensile strength | ISO 527-2 | 37.0 Mpa |
| Electrical performance | Test Condition | Test Method | DAICEL MALAYSIA/TF-30 CF2003 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 3E+13 ohms·cm | |
| Surface Resistivity | IEC 60093 | 5E+13 ohms |
| physical property | Test Condition | Test Method | DAICEL MALAYSIA/TF-30 CF2003 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 7.00 cm3/10min |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.80 % |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 8.0 g/10min |
| Thermal performance | Test Condition | Test Method | DAICEL MALAYSIA/TF-30 CF2003 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：23to55°C | 内部方法 | 1.4E-04 cm/cm/°C |
| MD：23到55°C | 内部方法 | 1.4E-04 cm/cm/°C |