SIS KRATON® D1161 E Kraton Polymers LLC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | Kraton Polymers LLC/KRATON® D1161 E |
|---|---|---|---|
| CouplingEfficiency | 内部方法 | 78to84 % |
| hardness | Test Condition | Test Method | Kraton Polymers LLC/KRATON® D1161 E |
|---|---|---|---|
| Shore hardness | 邵氏A,30秒,模压成型 | ISO 868 | 30 |
| elastomer | Test Condition | Test Method | Kraton Polymers LLC/KRATON® D1161 E |
|---|---|---|---|
| elongation | 断裂 | ISO 37 | 1300 % |
| tensile strength | 300%应变 | ISO 37 | 0.900 MPa |
| 屈服 | ISO 37 | 28.0 MPa |
| physical property | Test Condition | Test Method | Kraton Polymers LLC/KRATON® D1161 E |
|---|---|---|---|
| ash content | ESM | ISO 247 | 2.5to5.0 % |
| Apparent density | ASTM D1895B | 0.35 g/cm³ | |
| Solution viscosity | 内部方法 | 1200 mPa·s | |
| Extractable content | 内部方法 | <1.0 % | |
| density | ISO 2781 | 0.920 g/cm³ | |
| Polystyrene content | 内部方法 | 14to17 % | |
| Volatile compounds | 内部方法 | <0.30 % | |
| ash content | ET | ISO 247 | 0.10to0.40 % |
| ES | ISO 247 | 0.10to0.40 % | |
| melt mass-flow rate | 200°C/5.0kg | ISO 1133 | 9.0 g/10min |
| Antioxidants | 内部方法 | >0.060 % | |
| molecular weight distribution | 内部方法 | 207000to237000 g/mol | |
| ash content | EU | ISO 247 | <0.20 % |