PA6 TS250G8F5A 浙江新力
--
高流动性,低翘曲,热稳定,尺寸稳定,激光标识
塑壳断路器外壳,机内手柄
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | 浙江新力/TS250G8F5A |
|---|---|---|---|
| Tensile strength at break | IS0527 | 160 Mpa | |
| Yield bending strength | IS0178 | 260 Mpa | |
| Flexural modulus | IS0178 | 10000 Mpa | |
| elongation at break | IS0527 | 3.0 % | |
| Impact strength of simply supported beam without notch | IS0179 | 86 kJ/m² | |
| Charpy Notched Impact Strength | IS0179 | 16 kJ/m² |
| other | Test Condition | Test Method | 浙江新力/TS250G8F5A |
|---|---|---|---|
| proof tracking index | 3mm | IEC60112 | 250 V |
| Linear forming shrinkage rate | IS02577 | 0.4 % | |
| Surface Resistivity | IEC60093 | 1.00E+13 Q |
| Flame retardant performance | Test Condition | Test Method | 浙江新力/TS250G8F5A |
|---|---|---|---|
| Flame retardant performance UL94 | 厚度2.0mm | UL94 | ℃ |
| 厚度0.8mm | UL94 | ℃ | |
| 厚度1.5mm | UL94 | V-2 ℃ | |
| 厚度3.0mm | UL94 | ℃ |
| physical property | Test Condition | Test Method | 浙江新力/TS250G8F5A |
|---|---|---|---|
| density | IS01183 | 1.59 g/cm³ | |
| Water absorption rate | IS062 | 1.0 % |
| Thermal performance | Test Condition | Test Method | 浙江新力/TS250G8F5A |
|---|---|---|---|
| GWIT | 厚度3.0mm | IEC60695-2-13 | ℃ |
| GWFI | 厚度3.0mm | IEC60695-2-12 | ℃ |
| GWIT | 厚度1.5mm | IEC60695-2-13 | ℃ |
| 厚度0.8mm | IEC60695-2-13 | ℃ | |
| Hot deformation temperature 1.8MPa | IS076 | 200 ℃ | |
| Hot deformation temperature 0.45MPa | IS076 | ℃ | |
| GWFI | 厚度0.8mm | IEC60695-2-12 | ℃ |
| GWIT | 厚度2.0mm | IEC60695-2-13 | ℃ |
| GWFI | 厚度2.0mm | IEC60695-2-12 | ℃ |
| 厚度1.5mm | IEC60695-2-12 | 960 ℃ |