Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

POM 900P BK602 DUPONT USA
Delrin®
Fiber grade,Thin walled products
wear resistant,High rigidity,high strength,enhance,High impact resistance,High mobility
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | DUPONT USA/900P BK602 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
-30°C | ISO 179/1eA | 6.0 kJ/m² | |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 130 kJ/m² |
Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 7.0 kJ/m² |
-40°C | ISO 180/1A | 7.0 kJ/m² |
Supplementary Information | Test Condition | Test Method | DUPONT USA/900P BK602 |
---|---|---|---|
Emission | VDA275 | <8.00 mg/kg | |
Emissions of Organic Compounds | VDA277 | 4.30 µgC/g |
thermal performance | Test Condition | Test Method | DUPONT USA/900P BK602 |
---|---|---|---|
Linear coefficient of thermal expansion | TD:AnnealingTime-Optional | ISO 11359-2 | 30.0 min/mm |
Heat Deflection Temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 98.0 °C |
Linear coefficient of thermal expansion | TD:-40to23°C | ISO 11359-2 | 9.2E-05 cm/cm/°C |
Heat Deflection Temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 161 °C |
Linear coefficient of thermal expansion | TD:AnnealingTemperature | ISO 11359-2 | 160 °C |
TD:-- | ISO 11359-2 | 1E-04 cm/cm/°C | |
melting temperature | ISO 11357-3 | 178 °C | |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1E-04 cm/cm/°C |
MD:23到55°C | ASTME831 | 9.2E-07 cm/cm/°C |
Mechanical properties | Test Condition | Test Method | DUPONT USA/900P BK602 |
---|---|---|---|
Tensile modulus | ISO 527-2 | 3300 Mpa | |
Nominal tensile fracture strain | ISO 527-2 | 17 % | |
tensile strength | 屈服 | ISO 527-2 | 70.0 Mpa |
Tensile strain | 屈服 | ISO 527-2 | 12 % |
flexural modulus | ISO 178 | 3000 Mpa |
Physical properties | Test Condition | Test Method | DUPONT USA/900P BK602 |
---|---|---|---|
Water absorption rate | 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.40 % |
density | ISO 1183 | 1.42 g/cm³ | |
shrinkage rate | TD | ISO 294-4 | 1.7 % |
melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 25 g/10min |
shrinkage rate | MD | ISO 294-4 | 1.8 % |
flammability | Test Condition | Test Method | DUPONT USA/900P BK602 |
---|---|---|---|
UL flame retardant rating | 0.8mm | IEC 60695-11-10,-20 | HB |
1.5mm | IEC 60695-11-10,-20 | HB | |
FMVSS flammability | FMVSS302 | B | |
atomization | F-value(refraction) | ISO 6452 | 95 % |
G-value(condensate) | ISO 6452 | 2E-04 g | |
UL flame retardant rating | 0.8mm | UL 94 | HB |
1.5mm | UL 94 | HB | |
Limiting Oxygen Index | ISO 4589-2 | 23 % | |
burning rate | 1.00mm | ISO 3795 | 20 mm/min |