POM
POM JAPAN POLYPLASTIC P90XAP
Injection grade
US$ 2,307 / MT
FOB Guangzhou port, China
Electrical performanceTest ConditionTest MethodJAPAN POLYPLASTIC/P90XAP
Dielectric strength3.00mmIEC 60243-119 KV/mm
Volume resistivityIEC 600931E+14 ohms·cm
Surface resistivityIEC 600931E+16 ohms
mechanical propertiesTest ConditionTest MethodJAPAN POLYPLASTIC/P90XAP
bending strengthISO 17894.0 Mpa
Friction coefficientDynamic2JISK72180.37
Steel - Dynamic3JISK72180.40
Tensile modulusISO 527-22950 Mpa
Nominal tensile fracture strainISO 527-230 %
Wear factor0.98MPa,0.30m/sec5JISK721880 10^-8mm³/N·m
0.98MPa,0.30m/sec4JISK7218<1.0 10^-8mm³/N·m
Bending modulusISO 1782700 Mpa
tensile strengthISO 527-268.0 Mpa
impact performanceTest ConditionTest MethodJAPAN POLYPLASTIC/P90XAP
Charpy Notched Impact Strength23°CISO 179/1eA7.0 kJ/m²
Physical propertiesTest ConditionTest MethodJAPAN POLYPLASTIC/P90XAP
Water absorption rate23°C,24hrISO 620.60 %
densityISO 11831.41 g/cm³
Shrinkage rateTD:2.00mmISO 294-42.1 %
melt mass-flow rate190°C/2.16kgISO 11339.0 g/10min
Melt Volume Flow Rate (MVR)190°C/2.16kgISO 11338.00 cm3/10min
Shrinkage rateMD:2.00mmISO 294-41.9 %
flammabilityTest ConditionTest MethodJAPAN POLYPLASTIC/P90XAP
UL flame retardant ratingUL 94HB
Supplementary InformationTest ConditionTest MethodJAPAN POLYPLASTIC/P90XAP
ColourNumberCF2001
thermal performanceTest ConditionTest MethodJAPAN POLYPLASTIC/P90XAP
Linear coefficient of thermal expansionTD：23to55°CInternal Method1.1E-04 cm/cm/°C
MD：23to55°CInternal Method1.1E-04 cm/cm/°C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A100 °C
hardnessTest ConditionTest MethodJAPAN POLYPLASTIC/P90XAP
Rockwell hardnessM-ScaleISO 2039-290