Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 Generic Nylon 6 - Glass BeadGlass Fiber Generic
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Generic/Generic Nylon 6 - Glass BeadGlass Fiber |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 3.0to12 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 37to61 J/m |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 30to36 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 4.0to10 kJ/m² |
| Multi axis Instrumented Impact Energy | 23°C | ISO 6603-2 | 2.00to3.63 J |
| Multi axis Instrumented Peak Impact Force | 23°C | ISO 6603-2 | 700to813 N |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 34to46 kJ/m² |
| hardness | Test Condition | Test Method | Generic/Generic Nylon 6 - Glass BeadGlass Fiber |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 185 MPa |
| Electrical performance | Test Condition | Test Method | Generic/Generic Nylon 6 - Glass BeadGlass Fiber |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 | |
| relative permittivity | 23°C | IEC 60250 | 4.25 |
| dielectric strength | 23°C | IEC 60243-1 | 11to37 kV/mm |
| Dissipation Factor | 23°C | IEC 60250 | 0.013to0.027 |
| Volume resistivity | 23°C | IEC 60093 | 1.0E+13到2.5E+15 ohms·cm |
| Surface Resistivity | IEC 60093 | 1.0E+10到2.5E+14 ohms |
| Mechanical properties | Test Condition | Test Method | Generic/Generic Nylon 6 - Glass BeadGlass Fiber |
|---|---|---|---|
| elongation | 断裂,23°C | ISO 527-2 | 2.4to5.0 % |
| bending strength | 23°C | ASTM D790 | 130to200 MPa |
| tensile strength | 断裂,23°C | ASTM D638 | 116to125 MPa |
| Flexural modulus | 23°C | ISO 178 | 4690to5870 MPa |
| Tensile modulus | 23°C | ISO 527-2 | 4700to8890 MPa |
| 23°C | ASTM D638 | 6110to6210 MPa | |
| tensile strength | 断裂,23°C | ISO 527-2 | 92.6to125 MPa |
| Flexural modulus | 23°C | ASTM D790 | 4770to5810 MPa |
| bending strength | 23°C | ISO 178 | 144to186 MPa |
| elongation | 断裂,23°C | ASTM D638 | 2.0to4.0 % |
| flammability | Test Condition | Test Method | Generic/Generic Nylon 6 - Glass BeadGlass Fiber |
|---|---|---|---|
| Burning wire flammability index | IEC 60695-2-12 | 650to960 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 23to24 % |
| physical property | Test Condition | Test Method | Generic/Generic Nylon 6 - Glass BeadGlass Fiber |
|---|---|---|---|
| Shrinkage rate | 23°C | ISO 294-4 | 0.28to1.3 % |
| MD:23°C | ASTM D955 | 0.39to0.61 % | |
| density | 23°C | ISO 1183 | 1.34to1.37 g/cm³ |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 2.0to2.3 % |
| 饱和,23°C | ISO 62 | 6.5to7.1 % | |
| density | -- | ASTM D792 | 1.34to1.36 g/cm³ |
| Thermal performance | Test Condition | Test Method | Generic/Generic Nylon 6 - Glass BeadGlass Fiber |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 180to204 °C |
| 0.45MPa,未退火，HDT | ASTMD648 | 200to216 °C | |
| vicat | ISO 306 | 199to211 °C | |
| melting temperature | -- | ISO 11357-3 | 222 °C |
| -- | ISO 3146 | 220 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 189to192 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 3.0E-5到3.8E-5 cm/cm/°C |
| TD | ISO 11359-2 | 9E-05 cm/cm/°C |