Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
Unspecified ED223AE Borealis AG
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Borealis AG/ED223AE |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 70 kJ/m² |
| -30°C | ISO 179/1eA | 6.5 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Impact strength of cantilever beam gap | -20°C | ISO 180/1A | 13 kJ/m² |
| Charpy Notched Impact Strength | -20°C | ISO 179/1eA | 11 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 57 kJ/m² |
| Impact strength of simply supported beam without notch | -20°C | ISO 179/1eU | 220 kJ/m² |
| hardness | Test Condition | Test Method | Borealis AG/ED223AE |
|---|---|---|---|
| ball-indentation hardness | H132/10 | ISO 2039-1 | 31.0 MPa |
| Mechanical properties | Test Condition | Test Method | Borealis AG/ED223AE |
|---|---|---|---|
| Flexural modulus | ISO 178 | 1350 MPa | |
| Tensile strain | 断裂 | ISO 527-2/50 | >200 % |
| Tensile modulus | ISO 527-2/1 | 1300 MPa | |
| Tensile strain | 屈服 | ISO 527-2/50 | 7.0 % |
| tensile strength | 屈服 | ISO 527-2/50 | 16.0 MPa |
| bending strength | ISO 178 | 21.0 MPa |
| physical property | Test Condition | Test Method | Borealis AG/ED223AE |
|---|---|---|---|
| Shrinkage rate | --2 | 内部方法 | 0.80 % |
| density | ISO 1183 | 1.01 g/cm³ | |
| Shrinkage rate | 90°C,2小时 | 内部方法 | 0.10 % |
| melt mass-flow rate | 230°C/2.16kg | ISO 1133 | 9.0 g/10min |
| Thermal performance | Test Condition | Test Method | Borealis AG/ED223AE |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 89.0 °C |
| vicat | -- | ISO 306/A50 | 121 °C |
| -- | ISO 306/B50 | 38.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 49.0 °C |
| Linear coefficient of thermal expansion | MD：-30到80°C | 内部方法 | 5.1E-05 cm/cm/°C |