PBT 701SA EF2001 JAPAN POLYPLASTIC
DURANEX®
Automotive Applications
Glass fiber reinforced,low density,wear resistant,Low warpage,Filler: Glass fiber glass,30%,Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/701SA EF2001 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 80 |
| Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/701SA EF2001 |
|---|---|---|---|
| ColorNumber | EF2001/ED3002 |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/701SA EF2001 |
|---|---|---|---|
| bending strength | ISO 178 | 140 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.3 % |
| Flexural modulus | ISO 178 | 7000 Mpa | |
| tensile strength | ISO 527-2 | 96.0 Mpa |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/701SA EF2001 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| dielectric strength | 3.00mm | IEC 60243-1 | 22 KV/mm |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/701SA EF2001 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/701SA EF2001 |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 0.20 % |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/701SA EF2001 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：23to55°C | 内部方法 | 6E-05 cm/cm/°C |
| MD：23到55°C | 内部方法 | 3E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 180 °C |