PA66 A3 GF30 V0 OR2003/T-APC1 PA66 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Reference Price

PA66 CELANESE USA A3 GF30 V0 OR2003/T-APC1

Flame retardant enhanced grade

US$ 3,680 / MT

FOB Guangzhou port, China

mechanical properties	Test Condition	Test Method	CELANESE USA/A3 GF30 V0 OR2003/T-APC1
tensile strength	Yield, 23°C	ISO 527-2	135 Mpa
Tensile strain	Break, 23°C	ISO 527-2	2.5 %
Tensile modulus	23°C	ISO 527-2	10000 Mpa
thermal performance	Test Condition	Test Method	CELANESE USA/A3 GF30 V0 OR2003/T-APC1
Continuous use temperature		IEC 60216	130 °C
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	220 °C
Hot deformation temperature		1.8 MPa, Unannealed	ISO 75-2/A	210 °C
Ball Pressure Test	125°C	IEC 60695-10-2	通过
Ball Pressure Test		165°C	IEC 60695-10-2	通过
flammability	Test Condition	Test Method	CELANESE USA/A3 GF30 V0 OR2003/T-APC1
UL flame retardant rating	1.6 mm	UL 94	V-0
UL flame retardant rating		0.40 mm	UL 94	V-0
Extreme Oxygen Index		ISO 4589-2	30 %
Hot filament ignition temperature	3.2 mm	IEC 60695-2-13	800 °C
Hot filament ignition temperature		0.8 mm	IEC 60695-2-13	775 °C
UL flame retardant rating	0.8 mm	UL 94	V-0
UL flame retardant rating		3.2 mm	UL 94	V-0
Burning wire flammability index	3.2 mm	IEC 60695-2-12	960 °C
Burning wire flammability index		0.8 mm	IEC 60695-2-12	960 °C
Electrical performance	Test Condition	Test Method	CELANESE USA/A3 GF30 V0 OR2003/T-APC1
Needle flame test	1.00 mm	IEC 60695-11-5	通过
Volume resistivity	23°C	IEC 60093	1.0E+15 ohms·cm
Compared to the anti leakage trace index	3.20 mm, Solution A	IEC 60112	PLC 0
Needle flame test	2.00 mm	IEC 60695-11-5	通过
Surface resistivity		IEC 60093	1.0E+13 ohms
Dielectric strength	2.00 mm	IEC 60243-1	19 KV/mm
Physical properties	Test Condition	Test Method	CELANESE USA/A3 GF30 V0 OR2003/T-APC1
Water absorption rate	24 hr, 23°C	ISO 62	1.5 %
Water absorption rate		Saturation, 23°C	ISO 62	4.5 %
Shrinkage rate	Flow : 23°C	ISO 294-4	0.30 %
Shrinkage rate		横向Flow : 23°C	ISO 294-4	1.0 %
impact performance	Test Condition	Test Method	CELANESE USA/A3 GF30 V0 OR2003/T-APC1
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	无断裂