Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 A3 GF30 V0 OR2003/T-APC1 CELANESE USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE USA/A3 GF30 V0 OR2003/T-APC1 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/A3 GF30 V0 OR2003/T-APC1 |
|---|---|---|---|
| Tensile strain | 断裂, 23°C | ISO 527-2 | 2.5 % |
| tensile strength | 屈服, 23°C | ISO 527-2 | 135 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 10000 Mpa |
| Electrical performance | Test Condition | Test Method | CELANESE USA/A3 GF30 V0 OR2003/T-APC1 |
|---|---|---|---|
| dielectric strength | 2.00 mm | IEC 60243-1 | 19 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | 3.20 mm, 解决方案 A | IEC 60112 | PLC 0 |
| needle flame test | 2.00 mm | IEC 60695-11-5 | 通过 |
| Volume resistivity | 23°C | IEC 60093 | 1.0E+15 ohms·cm |
| Surface Resistivity | IEC 60093 | 1.0E+13 ohms | |
| needle flame test | 1.00 mm | IEC 60695-11-5 | 通过 |
| flammability | Test Condition | Test Method | CELANESE USA/A3 GF30 V0 OR2003/T-APC1 |
|---|---|---|---|
| Hot filament ignition temperature | 0.8 mm | IEC 60695-2-13 | 775 °C |
| UL flame retardant rating | 3.2 mm | UL 94 | V-0 |
| Burning wire flammability index | 0.8 mm | IEC 60695-2-12 | 960 °C |
| 3.2 mm | IEC 60695-2-12 | 960 °C | |
| UL flame retardant rating | 0.40 mm | UL 94 | V-0 |
| Hot filament ignition temperature | 3.2 mm | IEC 60695-2-13 | 800 °C |
| UL flame retardant rating | 0.8 mm | UL 94 | V-0 |
| 1.6 mm | UL 94 | V-0 | |
| Limiting Oxygen Index | ISO 4589-2 | 30 % |
| physical property | Test Condition | Test Method | CELANESE USA/A3 GF30 V0 OR2003/T-APC1 |
|---|---|---|---|
| Shrinkage rate | 横向流量 : 23°C | ISO 294-4 | 1.0 % |
| 流量 : 23°C | ISO 294-4 | 0.30 % | |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 1.5 % |
| 饱和, 23°C | ISO 62 | 4.5 % |
| Thermal performance | Test Condition | Test Method | CELANESE USA/A3 GF30 V0 OR2003/T-APC1 |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 220 °C |
| Continuous use temperature | IEC 60216 | 130 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 210 °C |
| ball-indentation hardness | 165°C | IEC 60695-10-2 | 通过 |
| 125°C | IEC 60695-10-2 | 通过 |