Plastomer, Ethylene-based Premi-Glas® 3101-25 USA Premix
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | USA Premix/Premi-Glas® 3101-25 |
|---|---|---|---|
| Clamping pressure | 3.45-6.89 MPa |
| Mechanical properties | Test Condition | Test Method | USA Premix/Premi-Glas® 3101-25 |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 124 MPa |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 690 J/m |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 530 J/m |
| tensile strength | 23°C | ASTM D638 | 33 MPa |
| Suspended wall beam without notch impact strength | 剪切模量 | 5200 MPa | |
| Tensile modulus | 23°C | ASTM D638 | 13400 MPa |
| Flexural modulus | 23°C | ASTM D790 | 11700 MPa |
| Suspended wall beam without notch impact strength | 泊松比 | 0.3 |
| Electrical performance | Test Condition | Test Method | USA Premix/Premi-Glas® 3101-25 |
|---|---|---|---|
| Dissipation Factor | 耐电弧性 | ASTM D495 | 210 sec |
| dielectric strength | ASTM D149 | 15 KV/mm |
| Flame retardant performance | Test Condition | Test Method | USA Premix/Premi-Glas® 3101-25 |
|---|---|---|---|
| UL flame retardant rating | UL -94 | V-0 1.60mm | |
| UL -94 | 5VB 2.60mm |
| physical property | Test Condition | Test Method | USA Premix/Premi-Glas® 3101-25 |
|---|---|---|---|
| Shrinkage rate | 比重 | 1.80-1.95 g/cm³ | |
| MD | ASTM D995 | 0.15 % | |
| TD | ASTM D995 | 0.30 % |
| Thermal performance | Test Condition | Test Method | USA Premix/Premi-Glas® 3101-25 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD | ASTM D696 | 3.5E-05 cm/cm／°C |
| Heat distortion temperature | 1.80MPa未退火，HDT | ASTM D648 | >=200 °C |
| Linear coefficient of thermal expansion | 加工温度 | 150 °C | |
| TD | ASTM D696 | 2.5E-05 cm/cm／°C | |
| 导热系数 | JISR2618 | 0.3 W/m/K |