TSU RapidCast™ RC-555 Innovative Polymers, Inc.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | Innovative Polymers, Inc./RapidCast™ RC-555 |
---|---|---|---|
Impact strength of cantilever beam gap | ASTM D256 | 59 J/m |
Mechanical properties | Test Condition | Test Method | Innovative Polymers, Inc./RapidCast™ RC-555 |
---|---|---|---|
Flexural modulus | ASTM D790 | 1280 MPa | |
bending strength | ASTM D790 | 51.7 MPa |
Uncured Properties | Test Condition | Test Method | Innovative Polymers, Inc./RapidCast™ RC-555 |
---|---|---|---|
Viscosity | 固化时间(25°C) | 24 hr | |
25°C4 | 1.2 Pa·s | ||
GelTime | 1.0to1.3 min | ||
25°C2 | 0.10 Pa·s | ||
25°C3 | 0.50 Pa·s |
thermosetting | Test Condition | Test Method | Innovative Polymers, Inc./RapidCast™ RC-555 |
---|---|---|---|
Thermosetting components | 脱模时间 | 10to15 min | |
硬化法 | 按重量计算的混合比:88按容量计算的混合比:100 | ||
树脂 | 按重量计算的混合比:100按容量计算的混合比:100 |
Cured Properties | Test Condition | Test Method | Innovative Polymers, Inc./RapidCast™ RC-555 |
---|---|---|---|
Shore hardness | ShoreD | ASTM D2240 | 70to80 |
elongation | 断裂 | ASTM D638 | 9.0 % |
tensile strength | ASTM D638 | 32.4 MPa |
physical property | Test Condition | Test Method | Innovative Polymers, Inc./RapidCast™ RC-555 |
---|---|---|---|
density | Hardener | 1.10 g/cm³ | |
基体树脂 | 1.26 g/cm³ | ||
Cured | 1.14 g/cm³ | ||
Shrinkage rate | MD | ASTM D2566 | 0.10to0.50 % |
Thermal performance | Test Condition | Test Method | Innovative Polymers, Inc./RapidCast™ RC-555 |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ASTM D648 | 90.0 °C |