PC FR6005 WH COVESTRO SHANGHAI
Makrolon®
Electronic and electrical
Easy to demould、Impact resistance、Aging resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | COVESTRO SHANGHAI/FR6005 WH |
|---|---|---|---|
| ISO 180 | 50 kJ/m² | ||
| Cantilever beam notch impact -30 ° C 3.0mm | ISO 180 | 15 kJ/m² | |
| Impact of simply supported beam gap at 23 ° C | ISO 179 | 68 kJ/m² | |
| Tensile modulus | 0mm/min | ISO 527 | 2300 Mpa |
| Maximum puncture resistance -30 ° C | ISO 6603 | 6100 N | |
| Maximum puncture resistance at 23 ° C | ISO 6603 | 5100 N | |
| Simply supported beam notch impact -30 ° C | ISO 179 | 20 kJ/m² | |
| Simply supported beam notch impact -10 ° C | ISO 179 | 50 kJ/m² | |
| Bending strength 2.0mm/min | ISO 178 | 90 Mpa | |
| ISO 178 | 2400 Mpa | ||
| Tensile strength yield 50mm/min | ISO 527 | 62 Mpa | |
| Tensile strength fracture 50mm/min | ISO 527 | 66 Mpa | |
| Cantilever beam notch impact at 23 ° C 3.0mm | ISO 180 | 60 kJ/m² | |
| Anti puncture 23 ° C | ISO 6603 | 54 J | |
| Elongation yield 50mm/min | ISO 527 | 6 % | |
| Elongation fracture 50mm/min | ISO 527 | 135 % | |
| Anti puncture -30 ° C | ISO 6603 | 55 J |
| Electrical performance | Test Condition | Test Method | COVESTRO SHANGHAI/FR6005 WH |
|---|---|---|---|
| Surface resistance | IEC 60093 | 400000000000000000 Ω | |
| CTI solution A | IEC 60112 | 200 V | |
| Volume resistance | IEC 60093 | 90000000000000000 Ω.m |
| Flame retardant performance | Test Condition | Test Method | COVESTRO SHANGHAI/FR6005 WH |
|---|---|---|---|
| Fire rating: Black 1.2mm | UL94 | V-0 | |
| ISO 11359-2 | 960 °C | ||
| Fire rating: Full color 1.5mm | UL94 | V-0 | |
| Fire rating: Full color 0.75mm | UL94 | V-2 | |
| Fire rating: Full color 3.0mm | UL94 | V-0 | |
| Fire rating: Black 1.0mm | UL94 | V-0 | |
| Heating wire ignition temperature 1.5mm | ISO 11359-2 | 850 °C | |
| Fire rating: Full color 1.2mm | UL94 | V-1 | |
| Heating wire ignition temperature 1.0mm | ISO 11359-2 | 875 °C | |
| Heating wire relative temperature 1.0mm | ISO 11359-2 | 850 °C |
| physical property | Test Condition | Test Method | COVESTRO SHANGHAI/FR6005 WH |
|---|---|---|---|
| Shrinkage rate flow | ISO 2577 | 0.6~0.8 % | |
| Vertical shrinkage rate | ISO 2577 | 0.6~0.8 % | |
| Specific gravity | ISO 1183 | 1200 kg/m3 | |
| melt mass-flow rate | 300°C 1.2kg | ISO 1133 | 9 cm3/10min |
| Thermal performance | Test Condition | Test Method | COVESTRO SHANGHAI/FR6005 WH |
|---|---|---|---|
| ISO 306 | 142 °C | ||
| Vertical coefficient of linear expansion 23~55 ° C | ISO 11359 | 0.000070 cm/cm/°C | |
| Vicat softening temperature 120 ° C/hr 50N | ISO 306 | 144 °C | |
| ISO 11359 | 0.000070 cm/cm/°C | ||
| ISO 75 | 121 °C | ||
| Hot deformation temperature 0.45MPa | ISO 75 | 136 °C | |
| Ball pressure test | ISO 11359-2 | 134 °C |