POM SW-01 POM vs. - Plastic Material Properties Comparison Chart at Plas.com

mechanical properties	Test Condition	Test Method	TAIWAN POLYPLASTICS/SW-01
bending strength		ISO 178	75.0 Mpa
Friction coefficient	Dynamic2	JISK7218	0.21
Wear factor	0.060MPa,0.15m/sec6	JISK7218	400 10^-8mm³/N·m
Wear factor		0.060MPa,0.15m/sec7	JISK7218	900 10^-8mm³/N·m
Friction coefficient	Steel - Dynamic3	JISK7218	0.14
Tensile modulus		ISO 527-2	2700 Mpa
Nominal tensile fracture strain		ISO 527-2	20 %
Wear factor	0.98MPa,0.30m/sec5	JISK7218	16 10^-8mm³/N·m
Wear factor		0.98MPa,0.30m/sec4	JISK7218	<1.0 10^-8mm³/N·m
Bending modulus		ISO 178	2500 Mpa
tensile strength		ISO 527-2	50.0 Mpa
Electrical performance	Test Condition	Test Method	TAIWAN POLYPLASTICS/SW-01
Dielectric strength	3.00mm	IEC 60243-1	18 KV/mm
Volume resistivity		IEC 60093	2E+14 ohms·cm
Physical properties	Test Condition	Test Method	TAIWAN POLYPLASTICS/SW-01
Water absorption rate	23°C,24hr	ISO 62	0.60 %
density		ISO 1183	1.42 g/cm³
Shrinkage rate	TD:2.00mm	ISO 294-4	1.7 %
melt mass-flow rate	190°C/2.16kg	ISO 1133	7.0 g/10min
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	6.00 cm3/10min
Shrinkage rate	MD:2.00mm	ISO 294-4	2.0 %
Supplementary Information	Test Condition	Test Method	TAIWAN POLYPLASTICS/SW-01
ColourNumber			CF2001/CD3501
thermal performance	Test Condition	Test Method	TAIWAN POLYPLASTICS/SW-01
Linear coefficient of thermal expansion	TD：23to55°C	Internal Method	1.1E-04 cm/cm/°C
Linear coefficient of thermal expansion		MD：23to55°C	Internal Method	1.1E-04 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	80.0 °C
impact performance	Test Condition	Test Method	TAIWAN POLYPLASTICS/SW-01
Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.4 kJ/m²
flammability	Test Condition	Test Method	TAIWAN POLYPLASTICS/SW-01
UL flame retardant rating		UL 94	HB
hardness	Test Condition	Test Method	TAIWAN POLYPLASTICS/SW-01
Rockwell hardness	M-Scale	ISO 2039-2	70