HDPE KPOL-HDPE HD K-0.65/964 KPOL Chem Co.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | KPOL Chem Co./KPOL-HDPE HD K-0.65/964 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D1822 | 126 kJ/m² |
| hardness | Test Condition | Test Method | KPOL Chem Co./KPOL-HDPE HD K-0.65/964 |
|---|---|---|---|
| Shore hardness | 邵氏D,1秒,23°C | ASTM D2240 | 65 |
| Mechanical properties | Test Condition | Test Method | KPOL Chem Co./KPOL-HDPE HD K-0.65/964 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | >300 % |
| tensile strength | 屈服 | ASTM D638 | 30.3 MPa |
| Flexural modulus | 3.20mm | ASTM D790 | 1650 MPa |
| physical property | Test Condition | Test Method | KPOL Chem Co./KPOL-HDPE HD K-0.65/964 |
|---|---|---|---|
| density | ASTM D1505 | 0.964 g/cm³ | |
| Environmental stress cracking resistance | 50°C,1.91mm,100%IgepalCO-630,F50 | ASTM D1693B | 8.00to10.0 hr |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.65 g/10min |
| Environmental stress cracking resistance | 50°C,3.18mm,100%IgepalCO-630,F50 | ASTM D1693A | 15.0to20.0 hr |
| Thermal performance | Test Condition | Test Method | KPOL Chem Co./KPOL-HDPE HD K-0.65/964 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 79.0 °C |
| vicat | ASTM D15256 | 130 °C | |
| brittle temperature | ASTM D746A | <-76.0 °C |