PA66 Sup-tech A601 Shanghai Suptech Engineering Plastics Co. Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Shanghai Suptech Engineering Plastics Co. Ltd./Sup-tech A601 |
|---|---|---|---|
| Charpy Notched Impact Strength | DIN 53453 | 6.0 kJ/m² |
| hardness | Test Condition | Test Method | Shanghai Suptech Engineering Plastics Co. Ltd./Sup-tech A601 |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 110 |
| Mechanical properties | Test Condition | Test Method | Shanghai Suptech Engineering Plastics Co. Ltd./Sup-tech A601 |
|---|---|---|---|
| Tensile strain | 断裂 | DIN 53452 | 40 % |
| tensile strength | 断裂 | DIN 53455 | 70.0 MPa |
| Flexural modulus | DIN 53457 | 2250 MPa | |
| bending strength | DIN 53457 | 90.0 MPa |
| Electrical performance | Test Condition | Test Method | Shanghai Suptech Engineering Plastics Co. Ltd./Sup-tech A601 |
|---|---|---|---|
| dielectric strength | DIN 53481 | 20 kV/mm | |
| Surface Resistivity | IEC 60093 | 1E+13 ohms |
| physical property | Test Condition | Test Method | Shanghai Suptech Engineering Plastics Co. Ltd./Sup-tech A601 |
|---|---|---|---|
| density | DIN 53479 | 1.09 g/cm³ | |
| Shrinkage rate | DIN 53464 | 0.013to0.016 % | |
| Water absorption rate | 饱和,23°C | DIN 53495 | 7.0 % |
| 23°C,24hr | DIN 53495 | 1.2 % |
| Thermal performance | Test Condition | Test Method | Shanghai Suptech Engineering Plastics Co. Ltd./Sup-tech A601 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | DIN 53461 | 70.0 °C |
| 熔融温度，HDT | DIN 53461 | 260 °C | |
| 0.45MPa,未退火，HDT | DIN 53461 | 200 °C |