Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA46 TS200F8 DSM HOLAND
Stanyl®
Fitness equipment、Home appliance components
Thermal stability、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DSM HOLAND/TS200F8 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 12 kJ/m² |
| -30°C | ISO 179/1eA | 11 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 80 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 12 kJ/m² |
| -40°C | ISO 180/1A | 11 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 65 kJ/m² |
| Mechanical properties | Test Condition | Test Method | DSM HOLAND/TS200F8 |
|---|---|---|---|
| tensile strength | 断裂, 160°C | ISO 527-2 | 100 Mpa |
| Tensile modulus | -- | ISO 527-2 | 10000 Mpa |
| tensile strength | 断裂, 180°C | ISO 527-2 | 95.0 Mpa |
| Tensile strain | 断裂, 120°C | ISO 527-2 | 7.5 % |
| tensile strength | 断裂 | ISO 527-2 | 210 Mpa |
| Flexural modulus | -- | ISO 178 | 9000 Mpa |
| Tensile modulus | 180°C | ISO 527-2 | 4400 Mpa |
| tensile strength | 断裂, 120°C | ISO 527-2 | 110 Mpa |
| Tensile modulus | 160°C | ISO 527-2 | 5000 Mpa |
| 120°C | ISO 527-2 | 5500 Mpa | |
| Tensile strain | 断裂, 200°C | ISO 527-2 | 7.5 % |
| Flexural modulus | 160°C | ISO 178 | 3900 Mpa |
| Tensile strain | 断裂, 180°C | ISO 527-2 | 7.5 % |
| 断裂 | ISO 527-2 | 4.0 % | |
| 断裂, 160°C | ISO 527-2 | 7.5 % | |
| Tensile modulus | 200°C | ISO 527-2 | 4000 Mpa |
| Flexural modulus | 120°C | ISO 178 | 4700 Mpa |
| tensile strength | 断裂, 200°C | ISO 527-2 | 90.0 Mpa |
| Electrical performance | Test Condition | Test Method | DSM HOLAND/TS200F8 |
|---|---|---|---|
| relative permittivity | 100 Hz | IEC 60250 | 4.40 |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 | |
| dielectric strength | IEC 60243-1 | 35 KV/mm | |
| Volume resistivity | IEC 60093 | 1.0E+15 ohms·cm | |
| relative permittivity | 1 MHz | IEC 60250 | 4.00 |
| flammability | Test Condition | Test Method | DSM HOLAND/TS200F8 |
|---|---|---|---|
| Flammability level | UL 94 | HB |
| physical property | Test Condition | Test Method | DSM HOLAND/TS200F8 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 2.6 % |
| density | ISO 1183 | 1.41 g/cm³ | |
| Shrinkage rate | 流量 | ISO 294-4 | 0.50 % |
| 横向流量 | ISO 294-4 | 1.3 % |
| Thermal performance | Test Condition | Test Method | DSM HOLAND/TS200F8 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 295 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 290 °C |
| RTI Elec | 0.8 mm | UL 746 | 65.0 °C |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 290 °C |
| Thermal Index - 5000 hr | IEC 60216 | 152 °C | |
| Linear coefficient of thermal expansion | 流动 | ISO 11359-2 | 2.5E-5 cm/cm/°C |
| 横向 | ISO 11359-2 | 6.0E-5 cm/cm/°C |