PC 4701R-70007 SABIC INNOVATIVE NANSHA

LEXAN™

Electronic and electrical components

High temperature resistan,transparent

--

--

--

--

--

--

--

--

--

--

--

--

--

--

--

Plastic Datasheets

hardness	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/4701R-70007
Rockwell hardness	M-Scale	ASTM D785	92
Rockwell hardness		R-Scale	ASTM D785	127

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/4701R-70007
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	148 °C
Linear coefficient of thermal expansion	-40 to 95°C，Flow	ASTM E831	8.1E-5 cm/cm/°C
RTI		UL 746	130 °C
RTI Elec		UL 746	130 °C
RTI Imp		UL 746	130 °C
specific heat		ASTM C351	1260 J/kg/°C
thermal conductivity		ASTM C177	0.21 W/m/K

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/4701R-70007
Bending modulus	50.0 mm Span	ASTM D790	2330 Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	97.0 Mpa
elongation	Break	ASTM D638	78 %
tensile strength	Yield	ASTM D638	65.0 Mpa
tensile strength		Break	ASTM D638	77.0 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/4701R-70007
Arc resistance		ASTM D495	PLC 6
Compared to the anti leakage trace index		UL 746	PLC 3
Dielectric constant	50 kHz	ASTM D150	3.27
		60 Hz	ASTM D150	3.27
		1 MHz	ASTM D150	3.10
Dielectric strength	3.20 mm, in Air	ASTM D149	20 KV/mm
Dissipation factor	60 Hz	ASTM D150	1.6E-3
		50 Hz	ASTM D150	1.6E-3
		100 Hz	ASTM D150	0.026
High arc combustion index		UL 746	PLC 3
High voltage arc tracing rate		UL 746	PLC 3
Hot wire ignition		UL 746	PLC 2
Volume resistivity		ASTM D257	> 2.5E+17 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/4701R-70007
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	2.0 g/10 min
melt mass-flow rate		300°C/6.1 kg	ASTM D1238	9.0 g/10 min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.80 - 1.0 %
Specific volume		ASTM D792	0.830 cm³/g
Water absorption rate	24 hr	ASTM D570	0.19 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/4701R-70007
Dart impact	23°C	ASTM D3029	149 J
Impact strength of cantilever beam gap		ASTM D1822	577 kJ/m²
Suspended wall beam without notch impact strength	23°C	ASTM D4812	3200 J/m

injection	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/4701R-70007
Back pressure			0.300 to 0.700 Mpa
drying temperature			120 °C
drying time			3.0 to 4.0 hr
Exhaust hole depth			0.025 to 0.076 mm
Mold temperature			80 to 115 °C
Processing (melt) temperature			350 to 370 °C
Screw speed			40 to 70 rpm
Spray nozzle temperature			345 to 365 °C
Suggested injection volume			40 to 60 %
Suggested maximum moisture content			0.020 %
Temperature at the front of the material cylinder			350 to 370 °C
Temperature at the rear of the barrel			325 to 350 °C
Temperature in the middle of the barrel			340 to 360 °C

optical performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/4701R-70007
Refractive index		ASTM D542	1.600
transmissivity	2540 μm	ASTM D1003	85.0 %
turbidity	2540 μm	ASTM D1003	1.0 %