Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TPV 111-35 CELANESE USA
Santoprene™
Electrical field、Electronic field、Bottle cap、Automotive sector、Printing machine parts、Phone、Architectural application、Washer、packing、sporting goods、Application in the automo
Aging resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | CELANESE USA/111-35 |
|---|---|---|---|
| Shore hardness | 邵氏A,15秒,23°C | ISO 868 | 38 |
| flammability | Test Condition | Test Method | CELANESE USA/111-35 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| elastomer | Test Condition | Test Method | CELANESE USA/111-35 |
|---|---|---|---|
| elongation | 断裂,23°C，横向 | ASTM D412 | 330 % |
| Tensile stress | 100%应变,23°C，横向流量 | ISO 37 | 1.00 Mpa |
| tensile strength | 断裂,23°C，横向流量 | ASTM D412 | 2.90 Mpa |
| elongation | 断裂,23°C，横向 | ISO 37 | 330 % |
| compression set | 23°C,22hr | ISO 815 | 10 % |
| tear strength | 23°C，Across Flow (横向) | ISO 34-1 | 10 kN/m |
| tensile strength | Break,23°C | ISO 37 | 2.90 Mpa |
| compression set | 125°C,70hr | ISO 815 | 31 % |
| tear strength | 23°C，横向流量 | ASTM D624 | 10.0 kN/m |
| Tensile stress | 100%应变,23°C，横向流量 | ASTM D412 | 1.00 Mpa |
| compression set | 23°C,22hr | ASTM D395B | 10 % |
| 125°C,70hr | ASTM D395B | 31 % |
| aging | Test Condition | Test Method | CELANESE USA/111-35 |
|---|---|---|---|
| mass change fraction | 23°C,168hr,inMethylethylketone | ASTM D471 | -41 % |
| Tensile stress change rate | 23°C,168hr,inAceticAcid，断裂 | ISO 1817 | -3.0 % |
| mass change fraction | 23°C,168hr,inDetergent(Tide),2.5% | ASTM D471 | 0.90 % |
| Shore hardness | ShoreA,23°C,168hr,inSodiumHydroxide,50% | ISO 1817 | 4.0 |
| Tensile stress change rate | 23°C,168hr,inIsopropylAlcohol，断裂 | ISO 1817 | 53 % |
| Change rate of tensile strength in air | 23°C,168hr,inIsopropylAlcohol | ISO 1817 | 27 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inSulfuricAcid,98% | ASTM D471 | -2.0 |
| ShoreA,23°C,168hr,inSodiumChloride,15% | ASTM D471 | 2.0 | |
| Change rate of ultimate elongation in air | 23°C,168hr,inSodiumChloride,15% | ASTM D471 | -7.0 % |
| Change rate of tensile strength in air | 23°C,168hr,inAceticAcid | ISO 1817 | -6.0 % |
| 23°C,168hr,inSodiumChloride,15% | ASTM D471 | -14 % | |
| Shore hardness | ShoreA,100°C,168hr,inDeionizedWater | ISO 1817 | 0.0 |
| mass change fraction | 23°C,168hr,inCyclohexane | ASTM D471 | -11 % |
| 23°C,168hr,inEthanol,95% | ASTM D471 | 0.20 % | |
| Change rate of tensile strength in air | 125°C,168hr,inIRM903Oil | ASTM D471 | -67 % |
| mass change fraction | 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | -0.30 % |
| Change rate of tensile strength in air | 125°C,168hr,inIRM903Oil | ISO 1817 | -67 % |
| Shore hardness | ShoreA,23°C,168hr,inSodiumChloride,15% | ISO 1817 | 2.0 |
| Change rate of hardness (Shore) in the air | ShoreA,125°C,168hr,inIRM903Oil | ASTM D471 | -30 |
| mass change fraction | 23.0°C,168hr,inSodiumChloride,15% | ISO 1817 | 0.10 % |
| Tensile stress change rate | 23°C,168hr,inSulfuricAcid,98%，断裂 | ISO 1817 | -10 % |
| mass change fraction | 23°C,168hr,inTrichloroethylene | ASTM D471 | -20 % |
| Change rate of tensile strength in air | 23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | -6.0 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inMethylethylketone | ASTM D471 | 15 |
| Change rate of tensile strength in air | 150°C,168hr | ISO 188 | -29 % |
| Shore hardness | ShoreA,23°C,168hr,inDetergent(Tide),2.5% | ISO 1817 | 2.0 |
| Tensile stress change rate | 125°C,70hr,inIRM903Oil，断裂 | ISO 1817 | -65 % |
| Change rate of tensile strength in air | 100°C,168hr,inIRM903Oil | ISO 1817 | -57 % |
| Tensile stress change rate | 100°C,168hr,inIRM903Oil，断裂 | ISO 1817 | -63 % |
| mass change fraction | 100°C,168hr,inIRM903Oil | ASTM D471 | 93 % |
| 23.0°C,168hr,inTrichloroethylene | ISO 1817 | -20 % | |
| Change rate of tensile strength in air | 23°C,168hr,inIsopropylAlcohol | ASTM D471 | 27 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inTrichloroethylene | ASTM D471 | 1.0 |
| mass change fraction | 23.0°C,168hr,inSodiumHydroxide,50% | ISO 1817 | -0.30 % |
| Shore hardness | ShoreA,23°C,168hr,inEthanol,95% | ISO 1817 | 1.0 |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inEthanol,95% | ASTM D471 | 1.0 |
| Shore hardness | ShoreA,125°C,168hr,inIRM903Oil | ISO 1817 | -30 |
| Change rate of tensile strength in air | 100°C,168hr,inDeionizedWater | ISO 1817 | -18 % |
| Change rate of ultimate elongation in air | 100°C,168hr,inIRM903Oil | ASTM D471 | -63 % |
| 23°C,168hr,inEthanol,95% | ASTM D471 | 3.0 % | |
| volume change | 125°C,70hr,在IRM903油中 | ASTM D471 | 110 % |
| Shore hardness | ShoreA,23°C,168hr,inAceticAcid | ISO 1817 | -1.0 |
| Change rate of ultimate elongation in air | 150°C,168hr | ASTM D573 | -1.0 % |
| Change rate of hardness (Shore) in the air | ShoreA,100°C,168hr,inIRM903Oil | ASTM D471 | -26 |
| mass change fraction | 23.0°C,168hr,inMethylethylketone | ISO 1817 | -41 % |
| Change rate of tensile strength in air | 23°C,168hr,inMethylethylketone | ASTM D471 | 43 % |
| 23°C,168hr,inSulfuricAcid,98% | ISO 1817 | -47 % | |
| 23°C,168hr,inDetergent(Tide),2.5% | ISO 1817 | -6.0 % | |
| 125°C,70hr,inIRM903Oil | ISO 1817 | -61 % | |
| Change rate of ultimate elongation in air | 23°C,168hr,inMethylethylketone | ASTM D471 | 80 % |
| mass change fraction | 23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | 0.20 % |
| Tensile stress change rate | 23°C,168hr,inTrichloroethylene，断裂 | ISO 1817 | 77 % |
| Change rate of tensile strength in air | 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | -5.0 % |
| 23°C,168hr,inAceticAcid | ASTM D471 | -6.0 % | |
| Shore hardness | ShoreA,23°C,168hr,inHydrochloricAcid,10% | ISO 1817 | -1.0 |
| Tensile stress change rate | 125°C,168hr,inIRM903Oil，断裂 | ISO 1817 | -70 % |
| Shore hardness | ShoreA,100°C,168hr,inIRM903Oil | ISO 1817 | -26 |
| Change rate of tensile strength in air | 23°C,168hr,inTrichloroethylene | ASTM D471 | 56 % |
| volume change | 125°C,70hr,在IRM903油中 | ISO 1817 | 110 % |
| Shore hardness | ShoreA,23°C,168hr,inIsopropylAlcohol | ISO 1817 | 5.0 |
| ShoreA,150°C,168hr | ISO 188 | -1.0 | |
| Tensile stress change rate | 100°C,168hr,inDeionizedWater，断裂 | ISO 1817 | -17 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | 0.0 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | 4.0 |
| Change rate of tensile strength in air | 150°C,168hr | ASTM D573 | -29 % |
| mass change fraction | 23.0°C,168hr,inDetergent(Tide),2.5% | ISO 1817 | 0.90 % |
| Tensile stress change rate | 23°C,168hr,inSodiumChloride,15%，断裂 | ISO 1817 | -7.0 % |
| mass change fraction | 23°C,168hr,inAceticAcid | ASTM D471 | 6.9 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inIsopropylAlcohol | ASTM D471 | 53 % |
| mass change fraction | 23.0°C,168hr,inAceticAcid | ISO 1817 | 6.9 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inHydrochloricAcid,10% | ASTM D471 | -1.0 |
| Change rate of tensile strength in air | 23°C,168hr,inHydrochloricAcid,10% | ISO 1817 | -6.0 % |
| Tensile stress change rate | 23°C,168hr,inDetergent(Tide),2.5%，断裂 | ISO 1817 | 0.0 % |
| Change rate of ultimate elongation in air | 125°C,168hr,inIRM903Oil | ASTM D471 | -70 % |
| Tensile stress change rate | 23°C,168hr,inEthanol,95%，断裂 | ISO 1817 | 3.0 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inTrichloroethylene | ASTM D471 | 77 % |
| Tensile stress change rate | 23°C,168hr,inCyclohexane，断裂 | ISO 1817 | 63 % |
| Shore hardness | ShoreA,23°C,168hr,inMethylethylketone | ISO 1817 | 15 |
| Change rate of tensile strength in air | 23°C,168hr,inTrichloroethylene | ISO 1817 | 56 % |
| mass change fraction | 125°C,168hr,inIRM903Oil | ISO 1817 | 100 % |
| Change rate of tensile strength in air | 23°C,168hr,inCyclohexane | ASTM D471 | 4040 % |
| 23°C,168hr,inEthanol,95% | ASTM D471 | -8.0 % | |
| 100°C,168hr,inDeionizedWater | ASTM D471 | -18 % | |
| mass change fraction | 23°C,168hr,inSulfuricAcid,98% | ASTM D471 | 7.2 % |
| Change rate of tensile strength in air | 100°C,168hr,inIRM903Oil | ASTM D471 | -57 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inCyclohexane | ASTM D471 | 63 % |
| Tensile stress change rate | 23°C,168hr,inSodiumHydroxide,50%，断裂 | ISO 1817 | -3.0 % |
| Change rate of ultimate elongation in air | 100°C,168hr,inDeionizedWater | ASTM D471 | -17 % |
| mass change fraction | 23.0°C,168hr,inIsopropylAlcohol | ISO 1817 | -25 % |
| 23.0°C,168hr,inHydrochloricAcid,10% | ISO 1817 | 0.20 % | |
| Change rate of ultimate elongation in air | 23°C,168hr,inDetergent(Tide),2.5% | ASTM D471 | 0.0 % |
| Change rate of tensile strength in air | 23°C,168hr,inSodiumChloride,15% | ISO 1817 | -14 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inDetergent(Tide),2.5% | ASTM D471 | 2.0 |
| Tensile stress change rate | 23°C,168hr,inHydrochloricAcid,10%，断裂 | ISO 1817 | 0.0 % |
| Change rate of tensile strength in air | 23°C,168hr,inCyclohexane | ISO 1817 | 4040 % |
| mass change fraction | 23.0°C,168hr,inCyclohexane | ISO 1817 | -11 % |
| Change rate of tensile strength in air | 23°C,168hr,inSulfuricAcid,98% | ASTM D471 | -47 % |
| mass change fraction | 23°C,168hr,inIsopropylAlcohol | ASTM D471 | -25 % |
| Hardness change rate in the air | ShoreA,150°C,168hr | ASTM D573 | -1.0 |
| mass change fraction | 23.0°C,168hr,inSulfuricAcid,98% | ISO 1817 | 7.2 % |
| Shore hardness | ShoreA,23°C,168hr,inSulfuricAcid,98% | ISO 1817 | -2.0 |
| mass change fraction | 100°C,168hr,inIRM903Oil | ISO 1817 | 93 % |
| Change rate of tensile strength in air | 23°C,168hr,inSodiumHydroxide,50% | ISO 1817 | -5.0 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | -3.0 % |
| mass change fraction | 100°C,168hr,inDeionizedWater | ASTM D471 | 6.2 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inSulfuricAcid,98% | ASTM D471 | -10 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inAceticAcid | ASTM D471 | -1.0 |
| ShoreA,23°C,168hr,inIsopropylAlcohol | ASTM D471 | 5.0 | |
| Change rate of ultimate elongation in air | 125°C,70hr,inIRM903Oil | ASTM D471 | -65 % |
| 23°C,168hr,inAceticAcid | ASTM D471 | -3.0 % | |
| Change rate of hardness (Shore) in the air | ShoreA,100°C,168hr,inDeionizedWater | ASTM D471 | 0.0 |
| Change rate of tensile strength in air | 125°C,70hr,inIRM903Oil | ASTM D471 | -61 % |
| mass change fraction | 23.0°C,168hr,inEthanol,95% | ISO 1817 | 0.20 % |
| Shore hardness | ShoreA,23°C,168hr,inTrichloroethylene | ISO 1817 | 1.0 |
| Tensile stress change rate | 23°C,168hr,inMethylethylketone，断裂 | ISO 1817 | 80 % |
| mass change fraction | 100°C,168hr,inDeionizedWater | ISO 1817 | 6.2 % |
| Shore hardness | ShoreA,23°C,168hr,inCyclohexane | ISO 1817 | -11 |
| Change rate of tensile strength in air | 23°C,168hr,inDetergent(Tide),2.5% | ASTM D471 | -6.0 % |
| mass change fraction | 125°C,168hr,inIRM903Oil | ASTM D471 | 100 % |
| Change rate of tensile strength in air | 23°C,168hr,inMethylethylketone | ISO 1817 | 43 % |
| mass change fraction | 23°C,168hr,inSodiumChloride,15% | ASTM D471 | 0.10 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inCyclohexane | ASTM D471 | -11 |
| Change rate of tensile strength in air | 23°C,168hr,inEthanol,95% | ISO 1817 | -8.0 % |
| Thermal performance | Test Condition | Test Method | CELANESE USA/111-35 |
|---|---|---|---|
| brittle temperature | ISO 812 | -63.0 °C | |
| ASTM D746 | -63.0 °C |