Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 B3EG5 BASF GERMANY
Ultramid®
Automotive sector
enhance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | BASF GERMANY/B3EG5 |
|---|---|---|---|
| Compared to the Leakage Traceability Index (CTI) | 干/湿 | 干/湿 | |
| Impact Strength | +23℃干/湿 | 10/30 J |
| Impact resistance | Test Condition | Test Method | BASF GERMANY/B3EG5 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 10.679to17.642 |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/B3EG5 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 12 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 2020 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 7400 kg/cm²(MPa)[Lb/in²] | |
| Tensile creep modulus | 1000h，湿 | 3000 Mpa | |
| Charpy Notched Impact Strength | +23℃，干/湿 | 12/25 KJ/m | |
| 30℃，干 | 75 KJ/m | ||
| Fracture stress (V=50mm/min) | 干/湿 | 160/105 Mpa | |
| Flexural modulus | 干/湿 | 7400/4200 Mpa | |
| ball-indentation hardness | 干/湿 | 210/140 Mpa | |
| elongation | ≤0.5%, +23℃，湿 | 3000 Mpa | |
| tensile strength | 断裂,23℃ | 95.17to284.83 MPa | |
| Charpy Notched Impact Strength | 30℃，干/湿 | 10 KJ/m | |
| Tensile modulus | 23℃ | 0.01.0.01E0.05-0.01.0.04E0.05 MPa | |
| elongation at break | ASTM D638/ISO 527 | 3.5 % | |
| Tensile yield stress (V=50mm/min) | 干/湿 | 160/105 Mpa | |
| Tensile strain | 断裂,23℃ | % | 2.5-3.0 |
| Tensile modulus | 干/湿 | 8000/5500 Mpa | |
| Charpy Notched Impact Strength | 干/湿 | 80/105 KJ/m | |
| Impact strength of cantilever beam gap | +23℃，干/湿 | 12/17 KJ/m | |
| Tensile modulus | ASTM D638/ISO 527 | 8000 kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 75 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | 干/湿 | 220/150 Mpa | |
| elongation at break | 干/湿，V=50mm/min | 3.5/8.5 % |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/B3EG5 |
|---|---|---|---|
| dielectric constant | 1MHz，干/湿 | 3.8/7 | |
| dielectric strength | K20/P50，干/湿 | 80/70 KV/mm | |
| dielectric constant | ASTM D150/IEC 60250 | 3.8 | |
| Surface Resistivity | 干/湿 | 10 Ω | |
| loss angle | 1MHz，干/湿 | 0.025/0.24 | |
| Volume resistivity | 干/湿 | 10 Ω.cm | |
| ASTM D257/IEC 60093 | 1E 13 Ω.cm |
| other | Test Condition | Test Method | BASF GERMANY/B3EG5 |
|---|---|---|---|
| characteristic | 高机械强度、刚度和热稳定性.低温抗冲击性 |
| Physical properties | Test Condition | Test Method | BASF GERMANY/B3EG5 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.35 % | |
| density | ASTM D792/ISO 1183 | 1320 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 55 （cm3/10min 275℃/5kg ) g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 6.8-7.4 % |
| physical property | Test Condition | Test Method | BASF GERMANY/B3EG5 |
|---|---|---|---|
| Shrinkage rate | 23℃ | % | 0.20-1.0 |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/B3EG5 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| TEMPERATURE | 在20000h/5000h，后拉伸强度下降50%时 | 120/150 °C | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 210(1.80MPa) ℃（℉） |
| Linear coefficient of thermal expansion | 23-80℃干态 | 2-2.5/6-7 | |
| Heat distortion temperature | 1.8MPa负荷，干态，HDT | 210 °C | |
| 1.8MPa,未退火，HDT | °C | 239to261 | |
| thermal conductivity | 干态 | 0.26 W/(m.K) | |
| Heat distortion temperature | 0.45MPa负荷，干态，HDT | 220 °C | |
| melting temperature | 220 ℃（℉） | ||
| maximum service temperature | 200 °C | ||
| specific heat | 干态 | 1.5 J/(g.K) | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 0.2-0.25 mm/mm.℃ |