density

23°C

ISO1183

g/cm³

1

Melt Volume-Flow Rate (MVR)

330°C/2.16kg

ISO1133

cm3/10min

1

Melt mass flow rate

330°C/2.16kg

ISO1133

g/10min

1

Shrinkage rate

TD:2.00mm

ISO294-4

%

0

Shrinkage rate

MD:2.00mm

ISO294-4

%

0

Water absorption rate

饱和,23°C

ISO62

%

0

Water absorption rate

平衡,23°C,50%RH

ISO62

%

0

Nominal tensile fracture strain

23°C

ISO527-2/50

%

>

Tensile modulus

23°C

ISO527-2/1

Mpa

2

tensile strength

屈服,23°C

ISO527-2/50

Mpa

7

Ball pressure hardness

ISO2039-1

Mpa

1

elongation

屈服,23°C

ISO527-2/50

%

6

Bending modulus

23°C

ISO178

Mpa

2

Bending strength

23°C

ISO178

Mpa

1

RTI Imp

UL746

°C

1

RTIElec

UL746

°C

1

RTIStr

UL746

°C

1

Hot deformation temperature

0.45MPa,未退火

ISO75-2/B

°C

1

Hot deformation temperature

1.8MPa,未退火

ISO75-2/A

°C

1

vicat softening point

ISO306/B120

°C

1

Linear coefficient of thermal expansion

MD：23到55°C

ISO11359-2

cm/cm/°C

6

Linear coefficient of thermal expansion

TD：23to55°C

ISO11359-2

cm/cm/°C

6

Surface resistivity

IEC60093

ohms

1

Dielectric strength

23°C,1.00mm

IEC60243-1

KV/mm

3

Leakage Trace Index

解决方案A

IEC60112

V

4

Leakage Trace Index

解决方案B

IEC60112

V

1

Volume resistivity

23°C

IEC60093

ohms·cm

1

Extreme Oxygen Index

ISO4589-2

%

2

Burning wire flammability index

IEC60695-2-12

°C

8

Light transmittance

1000µm

ISO13468-2

%

8