Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TPV 8201-90 CELANESE USA
Santoprene™
Kitchen utensils、Home appliance components、Fatigue relief supplies、Soft handle、Smart phone、Monitor、Fatigue relief supplies、Phone、Home appliance components、Monitor、Kitchen utensils、Soft handle
Low friction coefficient、Low mold expansion、Recyclable materials、Controllable mold expansi、Cleanable、Good melt strength、Good colorability、Ozone resistance、Chemical resistance、Low water absorption、Not absorbing water
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | CELANESE USA/8201-90 |
|---|---|---|---|
| Shore hardness | 邵氏A,15秒,23°C | ISO 868 | 94 |
| Electrical performance | Test Condition | Test Method | CELANESE USA/8201-90 |
|---|---|---|---|
| Hot wire ignition (HWI) | 1.6mm | UL 746 | PLC 3 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | 3.0mm | UL 746 | PLC 2 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | PLC | UL 746 |
| flammability | Test Condition | Test Method | CELANESE USA/8201-90 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | HB |
| 1.1mm | UL 94 | HB | |
| 1.6mm | UL 94 | HB |
| aging | Test Condition | Test Method | CELANESE USA/8201-90 |
|---|---|---|---|
| Shore hardness | ShoreA,23°C,168hr,inSodiumHydroxide,50% | ISO 1817 | 0.0 |
| Change rate of tensile strength in air | 23°C,168hr,在水中 | ISO 1817 | 1.0 % |
| Hardness change rate in the air | ShoreA,150°C,168hr | ASTM D573 | 1.0 |
| Change rate of ultimate elongation in air | 150°C,168hr | ASTM D573 | -15 % |
| mass change fraction | 23.0°C,168hr,inSulfuricAcid,98% | ISO 1817 | 1.0 % |
| Change rate of tensile strength in air | 23°C,168hr,inSulfuricAcid,98% | ISO 1817 | 4.0 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inSulfuricAcid,98% | ASTM D471 | 2.0 |
| Changes in air quality | 150°C,168hr | ASTM D573 | -7.0 % |
| Shore hardness | ShoreA,23°C,168hr,inSulfuricAcid,98% | ISO 1817 | 2.0 |
| Change rate of tensile strength in air | 23°C,168hr,inSodiumHydroxide,50% | ISO 1817 | -2.0 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inIRM903Oil | ASTM D471 | 2.0 % |
| 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | 0.0 % | |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inSodiumChloride,15% | ASTM D471 | 0.0 |
| Change rate of ultimate elongation in air | 23°C,168hr,inSodiumChloride,15% | ASTM D471 | -2.0 % |
| Change rate of tensile strength in air | 23°C,168hr,inIRM903Oil | ISO 1817 | -9.0 % |
| Change rate of ultimate elongation in air | 23°C,168hr,inSulfuricAcid,98% | ASTM D471 | 6.0 % |
| Change rate of tensile strength in air | 23°C,168hr,inSodiumChloride,15% | ASTM D471 | -1.0 % |
| mass change fraction | 23°C,168hr,inIRM903Oil | ASTM D471 | 18 % |
| Change rate of tensile strength in air | 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | -2.0 % |
| 23°C,168hr,inIRM903Oil | ASTM D471 | -9.0 % | |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inWater | ASTM D471 | -1.0 |
| mass change fraction | 23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | 2.0 % |
| Shore hardness | ShoreA,23°C,168hr,inSodiumChloride,15% | ISO 1817 | 0.0 |
| mass change fraction | 23.0°C,168hr,inSodiumChloride,15% | ISO 1817 | 1.0 % |
| Tensile stress change rate | 23°C,168hr,在水中，断裂 | ISO 1817 | 17 % |
| 23°C,168hr,inSulfuricAcid,98%，断裂 | ISO 1817 | 6.0 % | |
| Change rate of tensile strength in air | 23°C,168hr,在水中 | ASTM D471 | 1.0 % |
| mass change fraction | 23°C,168hr,inSulfuricAcid,98% | ASTM D471 | 1.0 % |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inIRM903Oil | ASTM D471 | -5.0 |
| Change rate of ultimate elongation in air | 23°C,168hr,在水中 | ASTM D471 | 17 % |
| Change rate of tensile strength in air | 150°C,168hr | ISO 188 | 1.0 % |
| Changes in air quality | 150°C,168hr | ISO 188 | -7.0 % |
| Tensile stress change rate | 23°C,168hr,inSodiumHydroxide,50%，断裂 | ISO 1817 | 0.0 % |
| mass change fraction | 23.0°C,168hr,inWater | ISO 1817 | -2.0 % |
| Shore hardness | ShoreA,150°C,168hr | ISO 188 | 1.0 |
| Change rate of hardness (Shore) in the air | ShoreA,23°C,168hr,inSodiumHydroxide,50% | ASTM D471 | 0.0 |
| Change rate of tensile strength in air | 23°C,168hr,inSodiumChloride,15% | ISO 1817 | -1.0 % |
| 150°C,168hr | ASTM D573 | 1.0 % | |
| mass change fraction | 23°C,168hr,在水中 | ASTM D471 | -2.0 % |
| Shore hardness | ShoreA,23°C,168hr,inIRM903Oil | ISO 1817 | -5.0 |
| mass change fraction | 23°C,168hr,inSodiumChloride,15% | ASTM D471 | 1.0 % |
| 23.0°C,168hr,inSodiumHydroxide,50% | ISO 1817 | 2.0 % | |
| Tensile stress change rate | 23°C,168hr,inIRM903Oil，断裂 | ISO 1817 | 2.0 % |
| Shore hardness | ShoreA,23°C,168hr,inWater | ISO 1817 | -1.0 |
| Tensile stress change rate | 23°C,168hr,inSodiumChloride,15%，断裂 | ISO 1817 | -2.0 % |
| Change rate of tensile strength in air | 23°C,168hr,inSulfuricAcid,98% | ASTM D471 | 4.0 % |
| mass change fraction | 23.0°C,168hr,inIRM903Oil | ISO 1817 | 18 % |
| elastomer | Test Condition | Test Method | CELANESE USA/8201-90 |
|---|---|---|---|
| elongation | 断裂,23°C，横向 | ASTM D412 | 620 % |
| Tensile stress | 100%应变,23°C，横向流量 | ISO 37 | 7.10 Mpa |
| tensile strength | 断裂,23°C，横向流量 | ASTM D412 | 13.0 Mpa |
| elongation | 断裂,23°C，横向 | ISO 37 | 620 % |
| tear strength | 23°C，Across Flow (横向) | ISO 34-1 | 48 kN/m |
| tensile strength | Break,23°C | ISO 37 | 13.0 Mpa |
| compression set | 70°C,22hr | ASTM D395B | 52 % |
| 70°C,22hr | ISO 815 | 52 % | |
| tear strength | 23°C，横向流量 | ASTM D624 | 48.0 kN/m |
| Tensile stress | 100%应变,23°C，横向流量 | ASTM D412 | 7.10 Mpa |
| Thermal performance | Test Condition | Test Method | CELANESE USA/8201-90 |
|---|---|---|---|
| brittle temperature | ISO 812 | -54.0 °C | |
| ASTM D746 | -54.0 °C | ||
| RTI Str | 1.6mm | UL 746 | 95.0 °C |
| 3.0mm | UL 746 | 95.0 °C | |
| 1.1mm | UL 746 | 90.0 °C | |
| RTI Elec | UL 746 | 100 °C |