PA6T E630NW1 MITSUI CHEM JAPAN
ARLEN™
Electrical applications、Electronic and electrical
Glass fiber reinforced、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | MITSUI CHEM JAPAN/E630NW1 |
|---|---|---|---|
| Rockwell hardness | M 级 | ASTM D785 | 100 |
| Mechanical properties | Test Condition | Test Method | MITSUI CHEM JAPAN/E630NW1 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 6.0 % |
| bending strength | ASTM D790 | 275 Mpa | |
| Flexural modulus | ASTM D790 | 12500 Mpa | |
| tensile strength | ASTM D638 | 210 Mpa |
| Electrical performance | Test Condition | Test Method | MITSUI CHEM JAPAN/E630NW1 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1.0E+15 ohms·cm | |
| dielectric constant | 1 MHz | ASTM D150 | 3.90 |
| dielectric strength | ASTM D149 | 24 KV/mm | |
| Dissipation Factor | 1 MHz | ASTM D150 | 0.013 |
| flammability | Test Condition | Test Method | MITSUI CHEM JAPAN/E630NW1 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| physical property | Test Condition | Test Method | MITSUI CHEM JAPAN/E630NW1 |
|---|---|---|---|
| Shrinkage rate | 流动 | ASTM D955 | 0.20 % |
| Water absorption rate | 24 hr, 23°C, 65%r.h | ASTM D570 | 2.1 % |
| Shrinkage rate | 横向流动 | ASTM D955 | 0.80 % |
| Thermal performance | Test Condition | Test Method | MITSUI CHEM JAPAN/E630NW1 |
|---|---|---|---|
| Glass Transition Temperature | 95.0 °C | ||
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ASTM D648 | 310 °C |
| melting temperature | 320 °C | ||
| Linear coefficient of thermal expansion | 横向 | ASTM E831 | 6.8E-5 cm/cm/°C |
| 流动 | ASTM E831 | 1.6E-5 cm/cm/°C |