Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI 2212EPR-1000 SABIC INNOVATIVE US
ULTEM™
Tool handle,Home appliance components,Automotive Interior Parts,Electrical equipment
Middle flow
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/2212EPR-1000 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 480 J/m |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 12.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/2212EPR-1000 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 5790 Mpa | |
| elongation | 断裂 | ASTM D638 | 3.0 % |
| bending strength | 断裂, 100 mm 跨距4 | ASTM D790 | 172 Mpa |
| elongation | 屈服 | ASTM D638 | 3.0 % |
| Flexural modulus | 100 mm 跨距4 | ASTM D790 | 5100 Mpa |
| tensile strength | 断裂 | ASTM D638 | 107 Mpa |
| 屈服 | ASTM D638 | 107 Mpa | |
| bending strength | 屈服, 50.0 mm 跨距3 | ASTM D790 | 172 Mpa |
| Flexural modulus | 50.0 mm 跨距3 | ASTM D790 | 5510 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/2212EPR-1000 |
|---|---|---|---|
| Hot wire ignition (HWI) | UL 746 | PLC 1 | |
| arc resistance | ASTM D495 | PLC 5 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 4 | |
| High arc combustion index (HAI) | UL 746 | PLC 4 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/2212EPR-1000 |
|---|---|---|---|
| UL flame retardant rating | 0.40 mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/2212EPR-1000 |
|---|---|---|---|
| Shrinkage rate | 横向流动 : 3.20 mm | 内部方法 | 0.50 - 0.70 % |
| melt mass-flow rate | 337°C/6.6 kg | ASTM D1238 | 15 g/10 min |
| Shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.50 - 0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/2212EPR-1000 |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 3.6E-5 cm/cm/°C |
| vicat | ASTM D15255 | 210 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 210 °C |
| 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 207 °C | |
| RTI Imp | UL 746 | 105 °C | |
| Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 7.2E-5 cm/cm/°C |
| RTI | UL 746 | 105 °C | |
| Heat distortion temperature | 0.45 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 212 °C |
| 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 205 °C | |
| RTI Elec | UL 746 | 105 °C |