PCTG DN001 EASTMAN USA
Eastar™
Electrical applications、Household daily necessiti
Chemical resistance、Hydrolysis resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | EASTMAN USA/DN001 |
---|---|---|---|
Impact strength of cantilever beam gap | -40°C | ASTM D256 | 64 J/m |
Multi axis Instrumented Impact Energy | -40°C,能量到力量峰值 | ISO 6603-2 | 16.0 J |
Impact strength of cantilever beam gap | 23°C | ISO 180 | 130 kJ/m² |
23°C | ASTM D4218 | NoBreak | |
-40°C | ISO 180 | 7.4 kJ/m² | |
23°C | ASTM D256 | NoBreak | |
-40°C | ASTM D4218 | NoBreak | |
Multi axis Instrumented Impact Energy | 23°C,能量到力量峰值 | ISO 6603-2 | 14.0 J |
hardness | Test Condition | Test Method | EASTMAN USA/DN001 |
---|---|---|---|
Rockwell hardness | R计秤,23°C | ASTM D785 | 105 |
Mechanical properties | Test Condition | Test Method | EASTMAN USA/DN001 |
---|---|---|---|
tensile strength | Yield,23°C,4.00mm | ISO 527-2 | 46.0 Mpa |
Tensile modulus | 23°C | ASTM D638 | 1800 Mpa |
tensile strength | 屈服,23°C | ASTM D638 | 45.0 Mpa |
断裂,23°C | ASTM D638 | 52.0 Mpa | |
Flexural modulus | 23°C,4.00mm | ISO 178 | 1800 Mpa |
Tensile strain | Break,23°C,4.00mm | ISO 527-2 | 230 % |
bending strength | 23°C,4.00mm | ISO 178 | 63.0 Mpa |
tensile strength | Break,23°C,4.00mm | ISO 527-2 | 47.0 Mpa |
elongation | 屈服,23°C | ASTM D638 | 5.0 % |
bending strength | 屈服,23°C | ASTM D790 | 66.0 Mpa |
Flexural modulus | 23°C | ASTM D790 | 1800 Mpa |
Tensile strain | Yield,23°C,4.00mm | ISO 527-2 | 4.4 % |
elongation | 断裂,23°C | ASTM D638 | 330 % |
Electrical performance | Test Condition | Test Method | EASTMAN USA/DN001 |
---|---|---|---|
dielectric constant | 23°C,1kHz | ASTM D150 | 2.70 |
23°C,1MHz | ASTM D150 | 2.50 | |
23°C,100kHz | ASTM D150 | 2.60 | |
Dissipation Factor | 23°C,1kHz | ASTM D150 | 5.6E-03 |
dielectric constant | 23°C,10kHz | ASTM D150 | 2.70 |
Dissipation Factor | 23°C,1MHz | ASTM D150 | 0.018 |
23°C,10kHz | ASTM D150 | 0.012 | |
23°C,100kHz | ASTM D150 | 0.016 | |
dielectric strength | 23°C | ASTM D149 | 16 KV/mm |
arc resistance | ASTM D495 | 66.0 sec |
flammability | Test Condition | Test Method | EASTMAN USA/DN001 |
---|---|---|---|
UL flame retardant rating | 3.2mm | UL 94 | HB |
1.6mm | UL 94 | HB |
physical property | Test Condition | Test Method | EASTMAN USA/DN001 |
---|---|---|---|
density | 23°C | ISO 1183 | 1.23 g/cm³ |
Shrinkage rate | MD:3.20mm | ASTM D955 | 0.20-0.50 % |
Water absorption rate | 23°C,24hr | ISO 62 | 0.13 % |
23°C,24hr | ASTM D570 | 0.13 % | |
density | ASTM D792 | 1.23 g/cm³ |
Thermal performance | Test Condition | Test Method | EASTMAN USA/DN001 |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ASTM D648 | 64.0 °C |
0.45MPa,未退火,HDT | ASTM D648 | 74.0 °C | |
specific heat | 240°C | 2050 J/kg/°C | |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/B | 74.0 °C |
specific heat | 导热系数(23°C) | 0.19 W/m/K | |
60°C | 1340 J/kg/°C | ||
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 65.0 °C |
vicat | ASTM D15252 | 88.0 °C | |
-- | ISO 306/B | 79.0 °C | |
-- | ISO 306/A | 88.0 °C |