ABS Elite HH 1891 Ineos ABS
--
Automotive Applications
Low glossiness
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Basic performance | Test Condition | Test Method | Ineos ABS/Elite HH 1891 |
---|---|---|---|
melt mass-flow rate | 220℃,10kg | ASTM D-1238 | 7.0 g/10min |
Melt volume flow rate | 220℃,10kg | ISO 1133 | 7.20 cm |
density | ISO 1183 | 1.06 g/cm | |
melt mass-flow rate | 230℃,3.8kg | ASTM D-1238 | 2.0 g/10min |
Mechanical properties | Test Condition | Test Method | Ineos ABS/Elite HH 1891 |
---|---|---|---|
Impact strength of cantilever beam gap | 23℃,3.18mm | ASTM D-256 | 192 J/m |
elongation | 断裂 | ASTM D-638 | 35 % |
Tensile modulus | 23℃ | ISO 527-1 | 2500 MPa |
bending strength | 23℃,屈服 | ASTM D-790 | 69.6 MPa |
tensile strength | 屈服,23℃ | ASTM D-638 | 42.1 MPa |
Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 11.0 KJ/m |
-30℃ | ISO 179/1eA | 5.90 KJ/m | |
Impact strength of cantilever beam gap | 23℃,6.35mm | ASTM D-256 | 128 J/m |
Charpy Notched Impact Strength | 23℃ | ISO 179/1eU | 70.0 KJ/m |
Impact strength of cantilever beam gap | 23℃,12.7mm | ASTM D-256 | 112 J/m |
Flexural modulus | 23℃ | ASTM D-790 | 2210 MPa |
Electrical performance | Test Condition | Test Method | Ineos ABS/Elite HH 1891 |
---|---|---|---|
Volume resistivity | IEC 60093 | 1E+15 ohm.cm | |
Surface Resistivity | IEC 60093 | 1E+15 ohms |
physical property | Test Condition | Test Method | Ineos ABS/Elite HH 1891 |
---|---|---|---|
density | ASTM D-792 | 1.05 g/cm | |
Shrinkage rate | ASTM D-955 | 0.40-0.70 % |
Thermal performance | Test Condition | Test Method | Ineos ABS/Elite HH 1891 |
---|---|---|---|
Heat distortion temperature | 1.80MPa,未退火,12.7mm,HDT | ASTM D-648 | 100 ℃ |
0.45MPa,未退火,3.18mm,HDT | ASTM D-648 | 101 ℃ | |
Linear coefficient of thermal expansion | ASTM D-696 | 0.000079 cm/cm℃ | |
vicat | Rate B,Loading 1(10N) | ASTM D-1525 | 117 ℃ |
Heat distortion temperature | 1.80MPa,未退火,6.35mm,HDT | ASTM D-648 | 97.2 ℃ |
0.45MPa,HDT | ISO 75-1 | 101 ℃ | |
1.80MPa,未退火,3.18mm,HDT | ASTM D-648 | 86.1 ℃ | |
combustibility | 1.60mm | UL 94 | HB |