Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP Fiberfil® J-60/10/FR Canada Fiberfil
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | Canada Fiberfil/Fiberfil® J-60/10/FR |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 100-110 R |
| Mechanical properties | Test Condition | Test Method | Canada Fiberfil/Fiberfil® J-60/10/FR |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 68.9 MPa |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 74.7 J/m |
| 屈服伸长率 | ASTM D638 | 3.0 % | |
| Tensile modulus | 23°C | ASTM D638 | 4140 MPa |
| Flexural modulus | 23°C | ASTM D790 | 3450 MPa |
| elongation at break | 23°C | ASTM D638 | 6.0 % |
| tensile strength | 屈服,23°C | ASTM D638 | 55.2 MPa |
| Flame retardant performance | Test Condition | Test Method | Canada Fiberfil/Fiberfil® J-60/10/FR |
|---|---|---|---|
| UL flame retardant rating | UL -94 | V-0 1.60mm |
| physical property | Test Condition | Test Method | Canada Fiberfil/Fiberfil® J-60/10/FR |
|---|---|---|---|
| melt mass-flow rate | 收缩率 | ASTM D995 | 0.50 % |
| Water absorption rate | (23°C,24hr) | ASTM D570 | 0.030 % |
| density | ASTM D792 | 1.37 g/cm³ | |
| melt mass-flow rate | ℃/Kg | ASTM D1238 | 8.0 g/10min |
| Shrinkage rate | MD,3.17mm | ASTM D995 | 0.40 % |
| Thermal performance | Test Condition | Test Method | Canada Fiberfil/Fiberfil® J-60/10/FR |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa未退火，HDT | ASTM D648 | 138 °C |
| 0.45MPa未退火，HDT | ASTM D648 | 143 °C |