PBT/PTFE D2000-GYL SABIC INNOVATIVE NANSHA
LNP™ LUBRICOMP™
Electrical appliances、Plastic bag、Aerospace Applications
wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/D2000-GYL |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C4 | ISO 180/1U | 140 kJ/m² |
| Dart impact | 23°C, Energy at Peak | ASTM D3763 | 40.0 J |
| -- | ISO 6603-2 | 45.0 J | |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 无断裂 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/D2000-GYL |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 1860 Mpa |
| elongation | 屈服 | ASTM D638 | 6.5 % |
| tensile strength | 断裂 | ASTM D638 | 60.0 Mpa |
| 断裂 | ISO 527-2 | 54.0 Mpa | |
| bending strength | -- | ISO 178 | 78.0 Mpa |
| Flexural modulus | ASTM D790 | 2130 Mpa | |
| coefficient of friction | Dynamic | ASTM D3702 | 0.16 |
| elongation | 屈服 | ISO 527-2 | 5.6 % |
| 断裂 | ASTM D638 | 130 % | |
| bending strength | -- | ASTM D790 | 82.0 Mpa |
| tensile strength | 屈服 | ASTM D638 | 53.0 Mpa |
| 屈服 | ISO 527-2 | 51.0 Mpa | |
| coefficient of friction | Static | ASTM D3702 | 0.090 |
| Tensile modulus | -- | ISO 527-2/1 | 2120 Mpa |
| elongation | 断裂 | ISO 527-2 | 99 % |
| Wear factor | ASTM D3702 | 1.2E+7 10^-8 mm³/N·m |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/D2000-GYL |
|---|---|---|---|
| Shrinkage rate | 流动 : 24小时 | ASTM D955 | 0.70 - 0.90 % |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.18 % |
| Shrinkage rate | 流量 : 24小时 | ISO 294-4 | 0.70 - 0.90 % |
| Water absorption rate | 24 hr, 50% RH | ASTM D570 | 0.14 % |
| Shrinkage rate | 横向流量 : 24小时 | ISO 294-4 | 0.70 - 0.90 % |
| 横向流动 : 24小时 | ASTM D955 | 0.70 - 0.90 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/D2000-GYL |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ASTM E831 | 7.4E-5 cm/cm/°C |
| 横向 : -40°C | ISO 11359-2 | 7.4E-5 cm/cm/°C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距4，HDT | ISO 75-2/Af | 128 °C |
| 0.45 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 142 °C | |
| Linear coefficient of thermal expansion | 横向 : -40 到 40°C | ASTM E831 | 7.4E-5 cm/cm/°C |
| Heat distortion temperature | 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距4，HDT | ISO 75-2/Bf | 140 °C |
| 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 130 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/D2000-GYL |
|---|---|---|---|
| drying time | 4.0 hr | ||
| screw speed | 30 to 60 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 300 to 310 °C | ||
| Temperature at the rear of the barrel | 295 to 305 °C | ||
| Processing (melt) temperature | 305 to 315 °C | ||
| drying temperature | 100 °C | ||
| Temperature at the front of the material cylinder | 305 to 315 °C | ||
| Back pressure | 0.200 to 0.300 Mpa | ||
| Temperature | 65 to 95 °C |