TPO PRE-ELEC® PP 1351 Premix Oy
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodPremix Oy/PRE-ELEC® PP 1351
Charpy Notched Impact Strength-20°CASTM D2562.1 kJ/m²
Impact strength of cantilever beam gap23°CISO 1808.0 kJ/m²
Impact strength of simply supported beam without notch-20°CASTM D25632 kJ/m²
Charpy Notched Impact Strength23°CASTM D2568.4 kJ/m²
Impact strength of cantilever beam gap-20°CISO 1803.0 kJ/m²
Suspended wall beam without notch impact strength-20°CISO 18020 kJ/m²
Impact strength of simply supported beam without notch23°CASTM D256NoBreak
Charpy Notched Impact Strength23°CISO 1799.0 kJ/m²
Suspended wall beam without notch impact strength-20°C,4.00mmASTM D25621.0 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179NoBreak
Impact strength of cantilever beam gap-20°C,4.00mm，AreaASTM D2562.10 kJ/m²
23°C,4.00mm，AreaASTM D2568.41 kJ/m²
Impact strength of simply supported beam without notch-20°CISO 17932 kJ/m²
Suspended wall beam without notch impact strength23°CISO 180NoBreak
Charpy Notched Impact Strength-20°CISO 1792.0 kJ/m²
Suspended wall beam without notch impact strength23°C,4.00mmASTM D256NoBreak
hardnessTest ConditionTest MethodPremix Oy/PRE-ELEC® PP 1351
Shore hardness邵氏DASTM D224074
邵氏DISO 86874
邵氏AISO 86898
邵氏AASTM D224098
Mechanical propertiesTest ConditionTest MethodPremix Oy/PRE-ELEC® PP 1351
tensile strength ASTM D63822.0 MPa
Tensile strain屈服ISO 527-26.0 %
断裂,4.00mmISO 527-210 %
Flexural modulus4.00mmASTM D7901380 MPa
4.00mmISO 1781400 MPa
tensile strength 屈服ASTM D63825.0 MPa
屈服ISO 527-225.0 MPa
4.00mmISO 527-222.0 MPa
Electrical performanceTest ConditionTest MethodPremix Oy/PRE-ELEC® PP 1351
Surface ResistivityIEC 61340-2-31.0E+5to1.0E+8 ohms
Volume resistivity内部方法1.0E+3to1.0E+7 ohms·cm
physical property Test ConditionTest MethodPremix Oy/PRE-ELEC® PP 1351
Shrinkage rateMDASTM D9551.2to1.8 %
MDISO 294-41.2to1.8 %
densityASTM D7920.996 g/cm³
ISO 11830.990 g/cm³
melt mass-flow rate230°C/5.0kgISO 113328 g/10min
230°C/2.16kgISO 11336.0 g/10min
Thermal performanceTest ConditionTest MethodPremix Oy/PRE-ELEC® PP 1351
Heat distortion temperature1.8MPa,未退火，HDTASTM D648A47.8 °C
1.8MPa,未退火，HDTISO 75-2/Af48.0 °C
0.45MPa,未退火，HDTASTM D648B83.9 °C
vicat--ISO 306/A50148 °C
--ASTM D15253148 °C
--ASTM D1525482.2 °C
--ISO 306/B5082.0 °C
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/Bf84.0 °C