TPEE 3078HS DUPONT USA
Hytrel®
Automotive Applications、Fitness equipment、electrical equipment
Thermal stability、Aging resistance、UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | DUPONT USA/3078HS |
|---|---|---|---|
| Linear thermal expansion coefficient | MD | ISO11359-2 | 1.8E-04 cm/cm/°C |
| Glass Transition Temperature | ISO11357-2 | -60.0 °C | |
| Brittleness Temperature | ISO974 | -98.0 °C | |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 2.1E-04 cm/cm/°C |
| Melting Temperature | ISO11357-3 | 177 °C | |
| Effective Thermal Diffusivity | 5.44E-08 m²/s |
| Elastomers Properties | Test Condition | Test Method | DUPONT USA/3078HS |
|---|---|---|---|
| Tearing Strength | 横向流量 | ISO34-1 | 77 kN/m |
| 流量 | ISO34-1 | 80 kN/m |
| Hardness | Test Condition | Test Method | DUPONT USA/3078HS |
|---|---|---|---|
| Shore Hardness | 邵氏D,15秒 | ISO868 | 26 |
| 邵氏D | ISO868 | 30 |
| Mechanical Properties | Test Condition | Test Method | DUPONT USA/3078HS |
|---|---|---|---|
| Flexural Modulus | ISO178 | 21.0 Mpa | |
| Tensile Creep Modulus | 1000hr | ISO899-1 | 18.0 Mpa |
| Tensile Stress | 10%应变 | ISO527-2 | 1.80 Mpa |
| Tensile Strain | 断裂 | ISO527-2 | >300 % |
| Nominal Tensile Strain at Break | ISO527-2 | 900 % | |
| Tensile Stress | 断裂 | ISO527-2 | 24.0 Mpa |
| Tensile Modulus | ISO527-2 | 24.0 Mpa | |
| Tensile Creep Modulus | 1hr | ISO899-1 | 22.0 Mpa |
| Tensile Stress | 50%应变 | ISO527-2 | 5.00 Mpa |
| Physical | Test Condition | Test Method | DUPONT USA/3078HS |
|---|---|---|---|
| SpecificHeatCapacityofMelt | 2150 J/kg/°C | ||
| Moisture Absorption | 平衡,23°C,2.00mm,50%RH | ISO62 | 0.20 % |
| Melt Volume flow Rate | 190°C/2.16kg | ISO1133 | 5.00 cm3/10min |
| Melt Mass-Flow Rate | 190°C/2.16kg | ISO1133 | 5.0 g/10min |
| Moisture Absorption | 饱和,23°C,2.00mm | ISO62 | 0.80 % |
| MediumDensity | 0.940 g/cm³ | ||
| Modeling Shrinkage | TD | ISO294-4 | 0.60 % |
| MD | ISO294-4 | 0.60 % | |
| Moisture Absorption | 23°C,24hr | ISO62 | 0.50 % |
| ThermalConductivityofMelt | 0.15 W/m/K |
| Impact Properties | Test Condition | Test Method | DUPONT USA/3078HS |
|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak |
| 23°C | ISO179/1eU | NoBreak |
| Flammability | Test Condition | Test Method | DUPONT USA/3078HS |
|---|---|---|---|
| Burning Rate | 1.00mm | ISO3795 | <100 mm/min |
| FMVSS Flammability | FMVSS302 | B | |
| Flame Rating | 3.0mm | IEC60695-11-10,-20 | HB |
| 3.0mm | UL94 | HB | |
| Oxygen Index | ISO4589-2 | 19 % | |
| Flame Rating | 1.5mm | UL94 | HB |
| 1.5mm | IEC60695-11-10,-20 | HB |
| Electrical Properties | Test Condition | Test Method | DUPONT USA/3078HS |
|---|---|---|---|
| Dielectric Strength | IEC60243-1 | 18 KV/mm | |
| Volume Resistivity | IEC60093 | 1E+13 ohms·cm | |
| Surface Resistivity | IEC60093 | 1E+14 ohms | |
| Relative Permittivity | 1MHz | IEC60250 | 5.30 |
| 100Hz | IEC60250 | 5.40 | |
| Dissipation Factor? | 1MHz | IEC60250 | 0.015 |
| 100Hz | IEC60250 | 7E-03 |