Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS FR23 BK4051 SABIC INNOVATIVE CANADA
CYCOLAC™
--
Flame retardant、High mobility、Durable、Flame retardant、Good liquidity、Good resilience
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE CANADA/FR23 BK4051 |
|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 41.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE CANADA/FR23 BK4051 |
|---|---|---|---|
| Tensile modulus 2 | ASTM D638 | 2410 Mpa | |
| bending strength | 屈服, 50.0 mm 跨距 | ASTM D790 | 73.0 Mpa |
| Tensile strength 3 | 屈服 | ASTM D638 | 42.0 Mpa |
| Elongation rate 3 | 断裂 | ASTM D638 | 11 % |
| 屈服 | ASTM D638 | 2.1 % | |
| Tensile strength 3 | 断裂 | ASTM D638 | 35.0 Mpa |
| Flexural modulus | 50.0 mm 跨距 | ASTM D790 | 2720 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE CANADA/FR23 BK4051 |
|---|---|---|---|
| UL flame retardant rating | 2.5 mm | UL 94 | 5VB |
| 2.3 mm | UL 94 | V-0 |
| Filling analysis | Test Condition | Test Method | SABIC INNOVATIVE CANADA/FR23 BK4051 |
|---|---|---|---|
| melt viscosity | 200°C, 1000 sec^-1 | ASTM D3835 | 310 Pa·s |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE CANADA/FR23 BK4051 |
|---|---|---|---|
| melt mass-flow rate | 230°C/3.8 kg | ASTM D1238 | 6.8 g/10 min |
| Molten Volume Flow Rate (MVR) | 220°C/10.0 kg | ISO 1133 | 37.0 cm3/10min |
| melt mass-flow rate | 220°C/5.0 kg | ISO 1133 | 9.0 g/10 min |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.50 到 0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE CANADA/FR23 BK4051 |
|---|---|---|---|
| 横向 : -40 到 40°C | ASTM E831 | 7.9E-5 cm/cm/°C | |
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 72.0 °C |
| vicat | ASTM D15255 | 90.0 °C | |
| 流动 : -40 到 40°C | ASTM E831 | 7.9E-5 cm/cm/°C | |
| RTI Imp | UL 746 | 60.0 °C | |
| Thermal deformation temperature under load | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 83.0 °C |
| RTI | UL 746 | 60.0 °C | |
| RTI Elec | UL 746 | 60.0 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE CANADA/FR23 BK4051 |
|---|---|---|---|
| Processing (melt) temperature | 200 到 220 °C | ||
| drying temperature | 80 到 90 °C | ||
| Exhaust hole depth | 0.038 到 0.051 mm | ||
| Temperature at the front of the material cylinder | 200 到 215 °C | ||
| Suggested maximum moisture content | 0.10 % | ||
| Temperature in the middle of the barrel | 195 到 205 °C | ||
| Temperature | 50 到 70 °C | ||
| screw speed | 30 到 60 rpm | ||
| Temperature at the rear of the barrel | 170 到 180 °C | ||
| Back pressure | 0.300 到 0.700 Mpa | ||
| drying time | 2.0 到 4.0 hr | ||
| Suggested injection volume | 50 到 70 % | ||
| Spray nozzle temperature | 200 到 220 °C |