Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
LLDPE PF-0218D NOVA CANADA
NOVAPOL®
film、chip、container、Charger casing
high strength、High toughness、Easy to process
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Supplementary Information | Test Condition | Test Method | NOVA CANADA/PF-0218D |
|---|---|---|---|
| LowFrictionPuncture-BlownFilm | 25.0µm | 内部方法 | 290 J/cm |
| film | Test Condition | Test Method | NOVA CANADA/PF-0218D |
|---|---|---|---|
| tensile strength | Break,25µm,BlownFilm | ASTMD882 | 25.0 Mpa |
| Tensile strain | Break,25µm,BlownFilm | ASTMD882 | 700 % |
| Film thickness - tested | 25 µm | ||
| tensile strength | Yield,25µm,BlownFilm | ASTMD882 | 10.0 Mpa |
| Tensile strain MD | Break,25µm,BlownFilm | ASTMD882 | 660 % |
| ElmendorfTearStrength-MD | 25µm,BlownFilm | ASTMD1922 | 110 g |
| ElmendorfTearStrength-TD | 25µm,BlownFilm | ASTMD1922 | 330 g |
| Secant modulus -1% Decant, MD | 25µm,BlownFilm | ASTMD882 | 170 Mpa |
| Secant modulus -1% Decant, TD | 25µm,BlownFilm | ASTMD882 | 190 Mpa |
| Falling hammer impact | 25µm,吹塑薄膜 | ASTMD1709A | 100 g |
| optical performance | Test Condition | Test Method | NOVA CANADA/PF-0218D |
|---|---|---|---|
| gloss | 45°,25.0µm,吹塑薄膜 | ASTMD2457 | 43 |
| Haze ratio | 25.0µm,吹塑薄膜 | ASTMD1003 | 14 % |
| Physical properties | Test Condition | Test Method | NOVA CANADA/PF-0218D |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 0.918 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 2.0 g/10min |
| physical property | Test Condition | Test Method | NOVA CANADA/PF-0218D |
|---|---|---|---|
| melt mass-flow rate | 190°C/2.16kg | ASTMD1238 | 2.0 g/10min |