PEEK Latilub 88/10-10T Y/10 LATI S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LATI S.p.A./Latilub 88/10-10T Y/10 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 55 kJ/m² |
| Supplementary Information | Test Condition | Test Method | LATI S.p.A./Latilub 88/10-10T Y/10 |
|---|---|---|---|
| dimensional stability | 63.0 |
| Mechanical properties | Test Condition | Test Method | LATI S.p.A./Latilub 88/10-10T Y/10 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 6.0 % |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 75.0 MPa |
| coefficient of friction | Dynamic | ASTM D1894 | 0.20 |
| Wear factor | ASTM D3702 | 7E-07 mm³/Nm | |
| Tensile modulus | 23°C | ISO 527-2/1 | 4000 MPa |
| coefficient of friction | Static | ASTM D1894 | 0.25 |
| physical property | Test Condition | Test Method | LATI S.p.A./Latilub 88/10-10T Y/10 |
|---|---|---|---|
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 0.75to1.2 % |
| density | ISO 1183 | 1.37 g/cm³ | |
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 0.85to1.3 % |
| Thermal performance | Test Condition | Test Method | LATI S.p.A./Latilub 88/10-10T Y/10 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 240 °C |
| vicat | ISO 306/B50 | 285 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 165 °C |