Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT V3900WX SABIC INNOVATIVE US
VALOX™
Automotive sector、Charging station、Electronic and electrical、Lighting applications、Communication equipment、Wire and cable
High impact、Low warpage、Dimensional stability、High toughness、Weather resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/V3900WX |
|---|---|---|---|
| Vicat Softening Temperature | Rate B/5 | ISO 306 | 121 °C |
| Relative Temperature Index | UL 746B | 120 °C | |
| Vicat Softening Temperature | Rate B/50 | ASTM D1525 | 105 °C |
| Ball Indentation Temperature | Pass | IEC 60695-10-2 | 125 °C |
| Coefficient of Linear Thermal Expansion(Across Flow) | -40°C to 4 | ISO 11359-2 | 89.7 E-6 °C |
| Coefficient of Linear Thermal Expansion(Flow) | -40°C to 4 | ASTM E831 | 88.4 E-6 °C |
| Coefficient of Linear Thermal Expansion(Across Flow) | -40°C to 4 | ASTM E831 | 89.7 E-6 °C |
| Coefficient of Linear Thermal Expansion(Flow) | -40°C to 4 | ISO 11359-2 | 88.4 E-6 °C |
| Flammability Properties | Test Condition | Test Method | SABIC INNOVATIVE US/V3900WX |
|---|---|---|---|
| Flame Rating （5VA） | UL94 | 3 mm | |
| Glow Wire Flammability Index | IEC 60695-2-12 | 960 passes at | |
| Flame Rating | UL94 | 1.5 mm |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/V3900WX |
|---|---|---|---|
| Modeling Shrinkage(Across Flow) | flow, 3.2 | Internal | 0.7~1 |
| Moisture Absorption | 23°C / 50 | ISO 62 | 0.03 |
| Melt Volume flow Rate (265°C/2.16 kg) | ISO 1133 | 11 cm³/10 min | |
| Moisture Absorption | 23°C/sat | ISO 62 | 0.1 |
| Melt Mass-Flow Rate (266°C 5kg) | ASTM D1238 | 35 g/10min |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/V3900WX |
|---|---|---|---|
| Tensile Elongation?(Yield) | Type I, 50 | ASTM D638 | 5 |
| Tensile Elongation?(Break) | ASTM D638 | 250 | |
| Tensile Modulus | 1 mm/mi | ISO 527 | 2090 Mpa |
| Tensile Elongation?(Break) | 50 mm/m | ISO 527 | 42 |
| Tensile Modulus | 5 mm/mi | ASTM D638 | 2200 Mpa |
| Flexural Modulus | 2 mm/m | ISO 178 | 2130 Mpa |
| 1.3 mm/m | ASTM D790 | 2200 Mpa | |
| Tensile Strength(Yield) | Type I, 50 | ASTM D638 | 53 Mpa |
| Tensile Strength(Break) | 50 mm/m | ISO 527 | 40 Mpa |
| Tensile Elongation?(Yield) | 50 mm/m | ISO 527 | 4 |
| Tensile Strength(Yield) | Internal | 48 Mpa | |
| Tensile Elongation?(Break) | Type I, 50 | ASTM D638 | 50 |
| Tensile Strength(Break) | Type I, 50 | ASTM D638 | 43 Mpa |
| Tensile Strength(Yield) | 50 mm/m | ISO 527 | 51 Mpa |
| 2 mm/m | ISO 178 | 73 Mpa | |
| 1.3 mm | ASTM D790 | 80 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/V3900WX |
|---|---|---|---|
| Notched Izod Impact Strength (23℃) | ASTM D256 | 110 J/m | |
| Notched Izod Impact Strength 23℃ | ASTM D256 | 800 J/m | |
| Instrumented Dart Impact (23℃) | ASTM D3763 | 50 J | |
| Instrumented Dart Impact (-40℃) | ASTM D3763 | 50 J | |
| Charpy Notched Impact Strength (23°C) | V-notch | ISO 179/1eA | 52 kJ/m² |
| Notched Izod Impact Strength (23℃) | 80*10*4 | ISO 180/1A | 8 kJ/m² |
| Notched Izod Impact Strength 23℃ | 80*10*4 | ISO 180/1A | 45 kJ/m² |
| Electrical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/V3900WX |
|---|---|---|---|
| Glow Wire Flammability Index | IEC 60695-2-12 | 960 passes | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | 825 | |
| UL 746C | F1 | ||
| Glow Wire Ignition Temperature | IEC 60695-2-13 | 725 by VDE |